Abstract:Whereas freeze-drying is a widely used method to produce porous hydrogel scaffolds, the mechanisms of pore formation involved in this process remained poorly characterized. To explore this, we focused on a cross-linked polysaccharide-based hydrogel developed for bone tissue engineering. Scaffolds were first swollen in 0.025% NaCl then freeze-dried at low cooling rate, i.e. - 0.1 °C min-1, and finally swollen in solvents of increasing ionic strength. We found that scaffold's porous structure is strongly conditioned by the nucleation of ice. Electron cryo-microscopy of frozen scaffolds demonstrates that each pore results from the growth of one to a few ice grains. Most crystals were formed by secondary nucleation since very few nucleating sites were initially present in each scaffold (0.1 nuclei cm-3 °C-1). The polymer chains are rejected in the intergranular space and form a macro-network. Its characteristic length scale coincides with the ice grain size (160 <math>μm</math>) and is several orders of magnitude greater than the mesh size (90 nm) of the cross-linked network. After sublimation, the ice grains are replaced by macro-pores of 280 <math>μm</math> mean size and the resulting dry structure is highly porous, i.e. 93%, as measured by high-resolution X-ray tomography. In the swollen state, the scaffold mean pore size decreases in solvent of increasing ionic strength (120 µm in 0.025% NaCl and 54 µm in DBPS) but the porosity remains the same, i.e. 29% regardless of the solvent. Finally, cell seeding of dried scaffolds demonstrates that the pores are adequately interconnected to allow homogenous cell distribution.<h3>Statement of significance</h3>The fabrication of hydrogel scaffolds is an important research area in tissue engineering. Hydrogels are textured to provide a 3D-framework that is favorable for cell proliferation and/or differentiation. Optimum hydrogel pore size depends on its biological application. Producing porous hydrogels is commonly achieved through freeze-drying. However, the mechanisms of pore formation remain to be fully understood. We carefully analyzed scaffolds of a cross-linked polysaccharide-based hydrogel developed for bone tissue engineering, using state-of-the-art microscopic techniques. Our experimental results evidenced the shaping of hydrogel during the freezing step, through a specific ice-templating mechanism. These findings will guide the strategies for controlling the porous structure of hydrogel scaffolds.

Study on the Preparation and Properties of Porous Gelatin Scaffolds by Emulsion Freeze-drying Method

Cryo-copolymerization Preparation of Dextran-Hyaluronate Based Supermacroporous Cryogel Scaffolds for Tissue Engineering Applications

Precise Printing of Microfiber Scaffold with Gelatin Methacryloyl (gelma)/polyethylene Oxide (PEO) Bioink

Preparation of Aligned Porous Gelatin Scaffolds by Unidirectional Freeze-Drying Method.

Characteristics and Cell Growth Behavior of Gelatin/Polyvinyl Alcohol Porous Scaffolds

Preparation and characterization of three dimensional porous silk fibroin/gelatin composite scaffolds

Phase separation, pore structure, and properties of nanofibrous gelatin scaffolds

Preparation and Properties of Silk Fibroin/Gelatin Porous Scaffolds for Liver Tissue Engineering

Preparation of 3-D Porous Fibroin Scaffolds by Freeze Drying with Treatment of Methanol Solutions

Fabrication and Characterization of Gelatin/Polyvinyl Alcohol Composite Scaffold

Study on Freeze-drying Process of Natural Polymer Porous Scaffolds

Preparation of Porous Polycaprolactone Scaffolds by Using Freeze-Drying Combined Porogen-Leaching Methods

Fabrication of Gelatin-Hyaluronic Acid Hybrid Scaffolds with Tunable Porous Structures for Soft Tissue Engineering.

Novel Porous Gelatin Scaffolds by Overrun/particle Leaching Process for Tissue Engineering Applications

Interpenetrating Polymer Network Hydrogels Composed of Chitosan and Photocrosslinkable Gelatin with Enhanced Mechanical Properties for Tissue Engineering

3D Bioplotting of Gelatin/Alginate Scaffolds for Tissue Engineering: Influence of Crosslinking Degree and Pore Architecture on Physicochemical Properties

Preparation of 3-D Regenerated Fibroin Scaffolds with Freeze Drying Method and Freeze Drying/foaming Technique

Mechanisms of pore formation in hydrogel scaffolds textured by freeze-drying

3D Macroporous Nanofibrous Scaffolds of Gelatin Made by One-step Crosslink in Ethanol Bath

Study of gelatin-containing artificial skin V: fabrication of gelatin scaffolds using a salt-leaching method

Fabrication, Characterization, and Biocompatibility Study of Gelatin-Blended Fibroin Scaffold