A Novel Approach for Separation and Recovery of Titanium, Scandium, Iron from Acidic Wastewater and Red Gypsum Utilization
Jinrong Ju,Yali Feng,Haoran Li,Ben Wang
DOI: https://doi.org/10.1007/s42461-022-00600-5
2022-04-21
Abstract:At present, acidic wastewater is directly neutralized with lime or limestone, which wastes resources such as titanium, scandium, and iron and generates a great deal of solid waste. This study proposes a novel approach for the separation and recovery of titanium, scandium, and iron from acidic wastewater and red gypsum utilization. The recovery efficiency of titanium in acidic wastewater was 97.59% under the molar ratio of titanium dioxide to phosphoric acid of 1:2.2, the reaction temperature of 85 °C, and the reaction time of 45 min. The scandium in the filtrate after the recovery of titanium can be finely extracted with P507, and 99.79% scandium can be extracted by single-stage extraction under the P507 concentration of 15%, the phase ratio (O/A) of 1:13, and extraction time of 6 min. In addition, the process of extracting scandium with P507 is an exothermic reaction by thermodynamic analysis. The raffinate after extracting scandium can be used for leaching red gypsum. As a result, calcium sulfate with a purity of 98.34% and whiteness of 94.27% was obtained under the leaching temperature of 60℃, the leaching time of 30 min, and the ratio of raffinate volume to red gypsum mass (L/S) of 3.5:1. Subsequently, the 97.64% iron in the leaching solution was recovered by the ammonium jarosite precipitation process, and ammonium sulfate with a purity of 99.65% can be obtained. The process can competently be applied to recover titanium, scandium, and iron in acidic wastewater and resource treatment of red gypsum.