Abstract:Titanium dioxide nanotube array (TiO2 NTA) grown on titanium substrate has been fabricated as active photoelectrode for organic compound degradation. TiO2 NTA shows the tubewall-separated nanotube arrangement and anatase crystal structure. Transient photocurrent of 1.86 mA and open-circuit photovoltage of 0.26 V are determined to keep stable level under ultraviolet (UV) light irradiation, indicating its high photoelectrochemical activity. The cathodic polarization process causes more feasible electron transfer than the equilibrium process and anodic polarization process, which is consistent with the declining current response at an increasing positive potential. The photocatalytic activity of TiO2 NTA is fully evaluated through UV light-induced photocatalysis and photoelectrocatalysis degradation of organic dye X-3B as a reactant pollutant. The pseudo-first-order reaction rate constant is enhanced from 0.00346 min(-1) for photocatalysis to 0.00521 min(-1) for photoelectrocatalysis using Langmuir-Hinshelwood kinetic model of heterogeneous catalysis. The tubewall-separated nanotube structure could induce photoelectron directional transport and provide extra interspace for reactant organic molecule diffusion at accessible surface area. The positive potential applied on TiO2 NTA could further promote photoelectron-hole pair separation. Two strategies of photoelectron generation and photoelectron-hole separation are accordingly adopted to improve its electro-assisted photocatalytic activity. Therefore, the tubewall-separated TiO2 NTA could present the promising photoelectrocatalysis application.

Photoelectrocatalytic Performance of Ag/TiO_(2-x)N_x Nanotube

Photoelectrochemical Properties of Ag/TiO2 Electrodes Constructed Using Vertically Oriented Two-Dimensional TiO2 Nanosheet Array Films

Fabrication of Ag/TiO2 Nanotube Array with Enhanced Photo-Catalytic Degradation of Aqueous Organic Pollutant

Synthesis of Co3O4/Ag/TiO2 Nanotubes Arrays Via Photo-Deposition of Ag and Modification of Co3O4 (311) for Enhancement of Visible-Light Photoelectrochemical Performance

Electrodeposition preparation of Ag loaded N-doped TiO2 nanotube arrays with enhanced visible light photocatalytic performance

Enhanced visible light activity of Ag-loaded TiO 2 nanotube arrays by AC electrodeposition

Photoelectrocatalytic properties of Ag nanoparticles loaded TiO2 nanotube arrays prepared by pulse current deposition

Photoelectrochemical Performance of Tubewall‐separated Titanium Dioxide Nanotube Array Photoelectrode

Electrodeposition Preparation of Ag Nanoparticles Loaded TiO2 Nanotube Arrays with Enhanced Photocatalytic Performance

Photoelectrocatalytic Property of Titanium Based TiO_2 Nanotube Array Electrode

[Research of the Photoelectrocatalysis Degradation of Methylene Blue of TiO2 Nanotube Array Films Annealed in Oxygen Atmospheres].

Photoelectrochemical Property and Photocatalytic Activity of N-doped TiO2 Nanotube Arrays

Nitrogen-Doped TiO<sub><b>2</b></sub>Nanotube Arrays with Enhanced Photoelectrochemical Property

Nitrogen-Doped Tio2 Nanotube Arrays With Enhanced Photoelectrochemical Property

Fabrication of Uniformly Dispersed Ag Nanoparticles Loaded TiO 2 Nanotube Arrays for Enhancing Photoelectrochemical and Photocatalytic Performances under Visible Light Irradiation

Photoelectrocatalytic Property Of Titanium Based Tio2 Nanotube Array Electrode

Highly ordered anodic TiO 2 nanotube arrays and their stabilities as photo(electro)catalysts

Preparation and Ag-modification of anodized titania nanotube array and its photocatalytic activity

Enhanced Photoelectrocatalytic Degradation of Ammonia by in Situ Photoelectrogenerated Active Chlorine on TiO2 Nanotube Electrodes.

N-doped TiO2 Nanotube Array Photoelectrode for Visible-Light-induced Photoelectrochemical and Photoelectrocatalytic Activities

Nitrogen-Doped Tio2 Nanotube Array Films With Enhanced Photocatalytic Activity Under Various Light Sources