Effect of Wire Diameter on the Microstructure and <inline-formula><tex-math notation="LaTeX"> $J_{{\text{c}}}$</tex-math></inline-formula> Properties of Ba<sub>0.6</sub>K<sub>0.4</sub>Fe<sub>2</sub>As<sub>2</sub> Tapes

Zhe Cheng,Xianping Zhang,Chao Yao,Chiheng Dong,Dongliang Wang,He Huang,Shifa Liu,Yanwei Ma
DOI: https://doi.org/10.1109/TASC.2018.2796140
IF: 1.9489
2018-01-01
IEEE Transactions on Applied Superconductivity
Abstract:For Ba <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.6</sub> K <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.4</sub> Fe <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> As <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> (Ba-122) superconducting tapes, which are made of round wires by a flat rolling process, the final diameters of the wires are critical parameters for the transport critical current density (J <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">c</sub> ). X-ray diffraction and scanning electron microscopy analysis revealed that the degree of texture is stronger in the samples rolled from wires with larger diameters. The hardness test showed that the highest density is obtained in the tapes rolled from wires of 1.8 mm in diameter in which the highest J <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">c</sub> of 3.31 × 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">4</sup> A · cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-2</sup> at 4.2 K and 10 T was achieved. It is suggested that superior J <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">c</sub> performance can be obtained in the samples with both large texture degree and high core density. Enhancing the texture and density is one way if we want to make small sized tapes with high transport J <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">c</sub> .
What problem does this paper attempt to address?