Superhydrophobic and Recyclable Cellulose-Fiber-Based Composites for High-Efficiency Passive Radiative Cooling

Yanpei Tian,Hong Shao,Xiaojie Liu,Fangqi Chen,Yongsheng Li,Changyu Tang,Yi Zheng

DOI: https://doi.org/10.1021/acsami.1c04046

2021-05-05

Abstract:Passive daytime radiative cooling (PDRC) involves cooling down an object by simultaneously reflecting sunlight and thermally radiating heat to the cold outer space through the Earth's atmospheric window. However, for practical applications, current PDRC materials are facing unprecedented challenges such as complicated and expensive fabrication approaches and performance degradation arising from surface contamination. Herein, we develop scalable cellulose-fiber-based composites with excellent self-cleaning and self-cooling capabilities, through air-spraying ethanolic poly(tetrafluoroethylene) (PTFE) microparticle suspensions embedded partially within the microsized pores of the cellulose fiber to form a dual-layered structure with PTFE particles atop the paper. The formed superhydrophobic PTFE coating not only protects the cellulose-fiber-based paper from water wetting and dust contamination for real-life applications but also reinforces its solar reflectivity by sunlight backscattering. It results in a subambient cooling performance of 5 °C under a solar irradiance of 834 W/m² and a radiative cooling power of 104 W/m² under a solar intensity of 671 W/m². The self-cleaning surface of composites maintains their good cooling performance for outdoor applications, and the recyclability of the composites extends their life span after one life cycle. Additionally, dyed cellulose-fiber-based paper can absorb appropriate visible wavelengths to display specific colors and effectively reflect near-infrared lights to reduce solar heating, which synchronously achieves effective radiative cooling and esthetic varieties.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c04046?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c04046</a>.Reflectivity spectra of the original paper and dust-stained paper, and the composition analysis of the paper composites (Figure S1); SEM images of the original paper and the PTFE particles (Figure S2); contact angle and reflectivity spectra of the paper composites fabricated by different parameters (Figure S3); comparison between the original paper and the paper composites (Figure S4); angle- and polarization-dependent reflectivity spectra of the paper composites (Figure S5); FTIR spectra of the lignin and PTFE (Figure S6); complex refractive indices (Figure S7); light scattering validations of the paper fibers and PTFE particles (Figure S8); reflectivity spectra of the original paper and paper composites and their compositions in different forms (Figure S9); reflectivity comparison of the paper composites and the Black 3.0 painted paper (Figure S10); transmissivity spectra of different layers of paper (Figure S11); setup of the outdoor radiative cooling experiments (Figure S12); temperature tracking, power compensation data analysis and humidity and wind speed over the experimental period (Figure S13); external factors on the radiative paper composites performance (solar intensity and nonradiative heat transfer and atmospheric transmittance) (Figure S14); cooling ability comparison of the paper composites and basswood (Figure S15); humidity and wind speed over the experimental period (Figure S16); optical properties of the paper composites, basswood, and concrete (Figure S17); thermal conductivity comparison of the paper composites, basswood, and concrete (Figure S18); temperature as a function of the net cooling or heating power (Figure S19); mechanical strength tests of the paper composites (Figure S20); self-cleaning tests of the paper composites and water repellence performance of different common materials (Figure S21); photographs of the water contact angles on the paper composites (Figure S22); temperature, humidity, and wind speed over the experimental period (Figure S23); water immersion tests (Figure S24); raindrop tests (Figure S25); abrasion tests (Figure S26); micrograph analysis of the paper composites after abrasion tests (Figure S27); hydrophobic parameter of the paper composites and Photographs showing the water contact angles (Figure S28); spectra analysis after abrasion tests (Figure S29); harsh environment exposure of the paper composites (Figure S30); antiscratch tests and micrographs of the original and paper composites after scratch tests (Figure S31); tape peel-off tests (Figure S32); spectra analysis of the paper composites after the tape peel-off test and recyclability of the paper composites (Figure S33); average near-infrared and mid-infrared spectral properties and temperature variation of the cooling paper and dyed wood (Figure S34); side view of the setup for the dyed paper composites and dyed basswood outdoor experiment under the clear sky and the humidity, and wind speed over the experimental period (Figure S35); experimental radiative cooling performances reported in other literature (Table S1); physical p <p>-Abstract Truncated-</p>

materials science, multidisciplinary,nanoscience & nanotechnology