Flexible Daytime Radiative Cooling Enhanced by Enabling Three-Phase Composites with Scattering Interfaces between Silica Microspheres and Hierarchical Porous Coatings

Hongchen Ma,Liang Wang,Shuliang Dou,Haipeng Zhao,Min Huang,Zewen Xu,Xinyuan Zhang,Xiudong Xu,Aiqin Zhang,Huiyu Yue,Ghulam Ali,Caihua Zhang,Wenying Zhou,Yao Li,Yaohui Zhan,Cheng Huang

DOI: https://doi.org/10.1021/acsami.1c02145

2021-04-19

Abstract:Daytime radiative cooling has attracted considerable attention recently due to its tremendous potential for passively exploiting the coldness of the universe as clean and renewable energy. Many advanced materials with novel photonic micro/nanostructures have already been developed to enable highly efficient daytime radiative coolers, among which the flexible hierarchical porous coatings (HPCs) are a more distinguished category. However, it is still hard to precisely control the size distribution of the randomized pores within the HPCs, usually resulting in a deficient solar reflection at the near-infrared optical regime under diverse fabrication conditions of the coatings. We report here a three-phase (i.e., air pore-phase, microsphere-phase, and polymer-phase) self-assembled hybrid porous composite coating, which dramatically increases the average solar reflectance and yields remarkable temperature drops of ∼10 and ∼ 30 °C compared to the ambient circumstance and black paint, respectively, according to the rooftop measurements. Mie theory and Monte Carlo simulations reveal the origin of the low reflectivity of as-prepared two-phase porous HPCs, and the optical cooling improvement of the three-phase porous composite coatings is attributed to the newly generated interfaces possessing the high scattering efficiency between the hierarchical pores and silica microspheres hybridized with appropriate mass fractions. As a result, the hybrid porous composite approach enhances the whole performance of the coatings, which provides a promising alternative to the flexible daytime radiative cooler.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c02145?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c02145</a>.Macroscopic morphologies of HPCs with different thicknesses (Figure S1), home-made template for preparing homogeneous coatings (Figure S2), SEM images of the HPCs hybridized by silica microspheres (Figures S3 and S4), long-time continual rooftop temperature test and the accompanying meteorological conditions (Figure S5), and simulated reflection spectra using the Monte Carlo method (Figure S6) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c02145/suppl_file/am1c02145_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology