New Advance in Biorenewable FDCA-based Polyesters: Multiple Scale-Up from Lab Bench to Pilot Plant

Bo Wang,Zhu Tu,Xinyuan Zhang,Lin Sang,Wentao Chan,Lei Wang,Xinming Pu,Feng Ling,Min Qi,Zhiyong Wei

DOI: https://doi.org/10.1016/j.cej.2023.145911

IF: 15.1

2023-01-01

Chemical Engineering Journal

Abstract:To accelerate the industrialization of 2,5-furan dicarboxylic acid (FDCA) based polyesters, it is essential to investigate the properties of FDCA-based polyesters prepared through scale-up experiments. In this work, poly (ethylene furanoate) (PEF) and poly(trimethylene furanoate) (PTF) were synthesized through lab bench (100 mL flask), pilot plant (5 and 150 L steel reactors). Additionally, the solid-state polycondensation industry was applied to enhance the intrinsic viscosities ([eta]) of PEF and PTF to satisfy processing requirements in diverse fields, and the effect of the [eta] on the machining, mechanical, and barrier property were further investigated. The results demonstrated that the tensile strengths of PEF and PTF prepared by 150 L steel reactor were 33.3% and 39.2% higher than these of 100 mL flask, which is attributed to the large-scale reactor can provide more accurate control for temperature, vacuum pressure, and mechanical stirring, etc. Moreover, FDCA-based polyesters with a high [eta] have better proprieties. PEF and PTF demonstrated corresponding tensile strengths of 93.2 and 80.2 MPa and elastic modulus of 2.1 and 1.8 GPa when their [eta] value is greater than 0.9 dL/g. Simultaneously, PEF and PTF have high barrier property for oxygen (0.019 and 0.022 barrer), carbon dioxide (0.018 and 0.032 barrer), and water vapor barrier (2.7 x 10(-14) and 2.9 x 10(-14) g center dot cm/cm(2)center dot s center dot Pa). Subsequently, a pilot scale (3000 L steel reactor) was used to prepare ton-scale PEF resin, fully meeting the application and development of FDCA-based polyester. The obtained results establish an entirely novel foundation for achieving large-scale applications and provide guidance for the industrial scale-up of FDCA-based polyesters.