Abstract:Laser Powder Bed Fusion (LPBF) technique has broad prospects in lightweight structure designing and rapid manufacturing. In this study, solution treatment (ST), hot isostatic pressing (HIP), and HIP+ST were performed on crack-free LPBF Hastelloy X. The corresponding microstructure, precipitates, and mechanical properties after different heat treatments were compared to identify the critical factor affecting the fracture mechanisms at room and elevated temperature. The specimens exhibited a high recrystallization degree under all heat treatment conditions, which had little contribution to the performance differences. However, different holding time and cooling rate led to variations in carbide distribution. Granular M6C carbides were formed in ST specimens, while linear M23C6 carbides were formed in HIP specimens. In contrast, barely no carbides were observed in the HIP+ST specimen. At room temperature, all specimens showed similar tensile strength, while the ranking of elongation was HIP+ST=ST>HIP. The decreased elongation of the HIP specimen was attributed to the linear carbides at grain boundaries. However, the ranking of elongation was presented as HIP>HIP+ST>ST at high temperature. Carbides at grain boundaries coarsened and affected the crack propagation behaviors. The HIP specimen had appropriate carbide size, which restricted the crack propagation within a single grain boundary, forming wedge-shaped cracks. When the carbide was too small or oversized, crack propagated along the grain boundaries and reduced the plasticity. This work demonstrated that the carbide size was a critical factor for the performance control. In addition, the room temperature performance was insufficient for evaluating suitable heat treatment conditions for LPBF Hastelloy X.

The Optimization of Residual Stress in Arc Bridge Hastelloy X Components Fabricated by Laser Powder Bed Fusion

Residual stress of typical parts in laser powder bed fusion

Tailoring the microstructure and mechanical properties for Hastelloy X alloy by laser powder bed fusion via scanning strategy

In-situ control of residual stress and its distribution in a titanium alloy additively manufactured by laser powder bed fusion

Assessment of Residual Stresses in Laser Powder Bed Fusion Manufactured IN 625

A Framework for Simulating the Path-level Residual Stress in the Laser Powder Bed Fusion Process

Investigation of Microstructure and Failure Mechanisms at Room and Elevated Temperature of Hastelloy X Produced by Laser Powder-Bed Fusion

Effect of Powder Layer Thickness on Residual Stress in Laser Powder Bed Fusion of IN718

Effect of Surface Modification on the High Temperature Low Cycle Fatigue Performance of LPBF 316L Austenitic Steel

On the effect of laser powder-bed fusion process parameters on quasi-static and fatigue behaviour of Hastelloy X: A microstructure/defect interaction study

Mitigation of Residual Stress and Distortion of AlSi10Mg Parts Produced by Laser Powder Bed Fusion through a Proper Selection of Support Geometry

The effect of rescanning strategy on residual stress and deformation of laser-based powder bed fusion of 316L stainless steel thin-walled parts

Laser Powder Bed Fusion of Inconel 718: Residual Stress Analysis Before and After Heat Treatment

Effect of laser process parameters on thermal behavior and residual stress of high-strength aluminum alloy processed by laser powder bed fusion

Recrystallization effect on surface passivation of Hastelloy X alloy fabricated by laser powder bed fusion

Surface Residual Stress and Roughness Mapping for Different Build Locations in Laser Powder Bed Fusion of Maraging Steel

Breaking the tradeoff: multiscale optimization for lower cost, lower residual stress LPBF of SS316L

Microstructure and Fatigue Behavior of Laser-Powder Bed Fusion Austenitic Stainless Steel

Microstructure tailoring in laser powder bed fusion (L-PBF): Strategies, challenges, and future outlooks

Residual stress reduction in Ti-6Al-4V parts fabricated by laser-foil-printing process

Effect of the scanning strategy on microstructure and mechanical anisotropy of Hastelloy X superalloy produced by Laser Powder Bed Fusion