Abstract:Concrete facilities in the severe-cold areas of western China (salt lake environments and heavy saline soils) are seriously damaged by the multiple corrosion effects of freeze–thaw cycles and sulfate corrosion. Magnesium phosphate cement (MPC) cement-based material has become an ideal concrete structural component because of its superior performance. Because concrete structural repair materials are used in heavy-corrosion environments, their durability in those environments should also be considered. Regarding the salt-freezing resistance of MPC, the existing studies have all used a NaCl solution as the heat transfer medium. In addition to chlorine salt, sulfate, especially Na2SO4, is also common in typical use environments such as oceans, salt lakes, and groundwater. To evaluate the sulfate freeze–thaw resistance of potassium magnesium phosphate cement (MKPC) mortar, in this study the strength development, weight loss, and water absorption of MKPC mortar specimens subjected to different freeze–thaw cycles were tested and compared with those for Portland cement (P.O) mortar specimens of the same strength grade. The results showed that the P.O mortar specimen completely lost its strength after 75 cycles of rapid water freezing and thawing and 50 cycles of sodium sulfate solution (5%) freezing and thawing. However, the residual strength rating of the MKPC mortar specimen after 75 cycles of water freezing and thawing and 100 cycles of sodium sulfate solution freezing and thawing was higher than 75%. After 50 rapid freeze–thaw cycles in water and a 5% Na2SO4 solution, the P.O mortar specimen’s mass loss exceeded the 5% failure standard, whereas the mass loss of the MKPC mortar specimens was much less than 5%. Before the freeze–thaw cycles, the water absorption of the P.O mortar specimen was close to 8 times that of the MKPC mortar specimen, and after 50 water freeze–thaw cycles and 25 sulfate solution freeze–thaw cycles, the water absorption reached 4.88% and 5.68%, respectively. However, after 225 freeze–thaw cycles in water and the sulfate solution, the water absorption rates of MKPC mortar specimens were 2.91% and 2.51% respectively. The test and analysis results show that the freeze–thaw resistance of MKPC mortar was much higher than that of Portland cement mortar specimens. Those results provide a prerequisite for applying and expanding the use of MKPC-based materials in severe-cold areas of western China (salt lake and heavily saline soil environments).

Interfacial Debonding Mechanism of Magnesium Phosphate Cement Onto Old Concrete Substrates under Freeze-Thaw Conditions

Bond strength and interface characteristics between magnesium phosphate cement mortar and ordinary Portland cement concrete in a frigid environment

Volume Stability and Frost Resistance of High−Ductility Magnesium Phosphate Cementitious Concrete

Sulfate Freeze–Thaw Resistance of Magnesium Potassium Phosphate Cement Mortar

Water-resisting Performances and Mechanisms of Magnesium Phosphate Cement Mortars Comprising with Fly-Ash and Silica Fume

Bond Properties of Magnesium Phosphate Cement-Based Engineered Cementitious Composite with Ordinary Concrete

Experimental Study on a Novel Modified Magnesium Phosphate Cement Mortar Used for Rapid Repair of Portland Cement Concrete Pavement in Seasonally Frozen Areas

Hydration Products and Microstructural Properties Analysis of Magnesium Phosphate Cement Comprising with Industrial Residues

Effects of Temperature and Moisture on Concrete-PCM Interface Performance

Characterizing the Influencing Factors in a Novel Repairing Material for Concrete Structures by AC Impedance Spectroscopy

Thermodynamic study on the phase assemblage of MPC exposed to natural and accelerated carbonation conditions

Influence of Synthetic Limestone Sand on the Frost Resistance of Magnesium Potassium Phosphate Cement Mortar

The Role of Bauxite and Fly-Ash on the Water Stability and Microstructural Densification of Magnesium Phosphate Cement Composites

Influencing Mechanism of Mineral Admixtures on Rheological Properties of Fresh Magnesium Phosphate Cement

Magnesium phosphate cement-based engineered cementitious composites with polyethylene fibers: Performance improvement and design method

Preparation and Application of Self-Curing Magnesium Phosphate Cement Concrete with High Early Strength in Severe Cold Environments

Development and characterization of magnesium phosphate cement based ultra-high performance concrete

Influence of Supplementary Materials on the Early Age Hydration Reactions and Microstructural Progress of Magnesium Phosphate Cement Matrices

Mixed mode fracture properties of interface for composite MPC and cement concrete specimen with asymmetric semicircular bending beam

Effects of Bauxite Tailings and Sodium Silicate on Mechanical Properties and Hydration Mechanism of Magnesium Phosphate Cement

Hydration properties of magnesium phosphate cement paste mixed with metakaolin and silica fume