Volume Stability and Frost Resistance of High−Ductility Magnesium Phosphate Cementitious Concrete

Lijuan Chai,Zhonghua Yue,Zhichun Chen,Gaoyu Fan,Liuye Wang

DOI: https://doi.org/10.3390/ma17112522

IF: 3.4

2024-05-24

Materials

Abstract:To address the issue of pavement cracking due to brittle concrete in road and bridge engineering, this study explores the use of high−ductility magnesium phosphate cementitious concrete (HD−MPCC) for rapid repairs. The deformation and frost properties of HD−MPCC are analyzed to assess its suitability for this application. Deformation properties were tested for HD−MPCC specimens cured in both air and water. Subsequent tests focused on the frost performance and mechanical properties after freeze–thaw cycles. A mercury penetration technique was utilized to examine the pore structure. The findings reveal that the expansion deformation of HD−MPCC increases with curing age in both air and water conditions, and the quantitative relationship between the expansion deformation and curing age of HD−MPCC was analyzed. Additionally, the freeze–thaw cycles led to a decrease in mass loss, the relative dynamic elastic modulus, the ultimate tensile strength, the ultimate tensile strain, the flexural strength, and the peak deflection. The volume fraction of harmless and less harmful pores gradually decreased as the freeze–thaw cycle increased, while the volume fraction of more harmful pores increased, resulting in a decrease in the strength, ultimate tensile strain, and peak deflection.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper primarily addresses the issue of pavement cracking in road and bridge engineering caused by the brittleness of concrete, exploring the application potential of a High-Ductility Magnesium Phosphate Cementitious Concrete (HD-MPCC) for rapid repair. Specifically, the study focuses on the deformation performance of this new concrete material under air and water curing conditions, as well as its frost resistance and mechanical properties after freeze-thaw cycles, and characterizes its pore structure. The main problems the paper attempts to solve include: 1. **Deformation Performance**: Analyzing the expansion deformation behavior of HD-MPCC under different curing conditions and its relationship with curing time. 2. **Frost Resistance**: Evaluating the changes in mass loss, relative dynamic elastic modulus, ultimate tensile strength, ultimate tensile strain, flexural strength, and peak deflection of HD-MPCC after experiencing freeze-thaw cycles. 3. **Pore Structure Changes**: Using mercury intrusion porosimetry to investigate the changes in the pore structure of HD-MPCC after different numbers of freeze-thaw cycles. Through these studies, the paper aims to verify whether HD-MPCC is suitable for rapid repair applications in road and bridge engineering, particularly its feasibility in cold regions. Additionally, the paper explores how to prepare this high-ductility concrete using lower-cost raw materials to reduce its application cost in practical engineering.

Volume Stability and Frost Resistance of High−Ductility Magnesium Phosphate Cementitious Concrete

Mesoscale Simulation of Fatigue Behavior of Concrete Materials Damaged by Freeze-Thaw Cycles

Experimental Study on a Novel Modified Magnesium Phosphate Cement Mortar Used for Rapid Repair of Portland Cement Concrete Pavement in Seasonally Frozen Areas

Influence of Synthetic Limestone Sand on the Frost Resistance of Magnesium Potassium Phosphate Cement Mortar

Freezing and Thawing Durability of High Early Strength Portland Cement Concrete

Multi-scale Thermo-Poro-mechanical Simulation of the Frost Resistance of Low-Heat and Moderate-Heat Hydraulic Concrete Considering the Aging Microstructure

Experimental Examination of Electrical Characteristics for Portland Cement Mortar Frost Damage Evaluation

Durability and microstructural evolution of high-performance ecological geopolymer concrete under low-pressure–salt-erosion–freeze–thaw cycling conditions

Interfacial Debonding Mechanism of Magnesium Phosphate Cement Onto Old Concrete Substrates under Freeze-Thaw Conditions

Stress Analysis for Concrete Materials under Multiple Freeze-Thaw Cycles

Bond strength and interface characteristics between magnesium phosphate cement mortar and ordinary Portland cement concrete in a frigid environment

Development and characterization of magnesium phosphate cement based ultra-high performance concrete

Effect of Steel Fiber on Mechanical Properties and Microstructure of Magnesium Phosphate Cement-Based Concrete Exposed to Water and Sulfate Attack

Early-age Mechanical Properties and Hydration Degrees of Magnesium Phosphate Cement Paste in Freezing Winter of Cold Regions

Long-term Performance of Magnesium Phosphate Cement Concrete Prepared in the Winter

Investigation on Degradation of Micromechanical Properties of Interfacial Transition Zone of Ultra-High Performance Concrete under Freeze-Thaw Cycles

Experimental Study on Mechanical Properties and Pore Structure Deterioration of Concrete under Freeze–Thaw Cycles

Concrete Performance Using Low-Degradation Aggregates

Laboratory Freeze–thaw Assessment of Cement, Fly Ash, and Fiber Stabilized Pavement Foundation Materials

Study on Frost Resistance and Interface Bonding Performance through the Integration of Recycled Brick Powder in Ultra-High-Performance Concrete for Structural Reinforcement

Magnesium phosphate cement-based engineered cementitious composites with polyethylene fibers: Performance improvement and design method