Fast-charging Capability of Graphite-Based Lithium-Ion Batteries Enabled by Li 3 P-based Crystalline Solid–electrolyte Interphase

Shuibin Tu,Bao Zhang,Yan Zhang,Zihe Chen,Xiancheng Wang,Renming Zhan,Yangtao Ou,Wenyu Wang,Xuerui Liu,Xiangrui Duan,Li Wang,Yongming Sun

DOI: https://doi.org/10.1038/s41560-023-01387-5

IF: 56.7

2023-01-01

Nature Energy

Abstract:Li + desolvation in electrolytes and diffusion at the solid–electrolyte interphase (SEI) are two determining steps that restrict the fast charging of graphite-based lithium-ion batteries. Here we show that the low-solvent-coordination Li + solvation structure could be induced near the inner Helmholtz plane on inorganic species. Specifically, Li 3 P could enable a lower Li + desolvation barrier and faster Li + diffusion capability through the SEI in comparison to the regular SEI components. We construct an ultrathin S-bridged phosphorus layer on a graphite surface, which in situ converts to crystalline Li 3 P-based SEI with high ionic conductivity. Our pouch cells with such a graphite anode show 10 min and 6 min (6C and 10C) charging for 91.2% and 80% of the capacity, respectively, as well as 82.9% capacity retention for over 2,000 cycles at a 6C charging rate. Our work reveals the importance of the SEI component and structure regulation for fast-charging LIBs.