Microstructure and Mechanical Properties of TC4/Q235 Dual-Beam Laser Lap Joint Using Cu-Si Filler Wire

Wendong Zhang,Qiang Lang,Shuaishuai Chen,Shuyan Shi,Hongyang Wang,Liming Liu
DOI: https://doi.org/10.1016/j.optlastec.2023.109946
2024-01-01
Abstract:Continuous-pulse coaxial dual-beam laser technology was used to join titanium alloy TC4 and steel Q235 successfully. The formation of Ti-Fe IMCs was inhibited by adding Cu-Si wire and using dual-beam laser heat sources to precisely control the heat input. A Ti / Cu interface layer composed of Ti2Cu, TiCu and AlCu2Ti was formed between the weld and TC4 substrate. All joints fractured at the Ti / Cu interface layer. The mechanical properties of the joints were optimized by controlling laser offset (DO) and dual-beam laser power. The effects of different power combinations of continuous and pulse laser on the properties of the joints were studied. Compared to the combination of high continuous laser power (PC) and low pulse laser power (PP), the joint strength was found to be higher with the combination of low PC and high PP. The continuous laser mainly acts on the melting of the base metal and increasing the penetration depth. The pulse laser mainly acts on the stirring molten pool and promoting the flow of the molten pool. By using the combination of high PP and low PC, it is possible to prevent the combination of Ti and Fe due to less melting of the base metal, resulting in a joint with a lower thickness and a higher width of the Ti / Cu interface layer. The joint exhibits excellent mechanical properties.
What problem does this paper attempt to address?