Microstructure and mechanical property improvement of Ti alloy and stainless steel joint based on a hybrid connection mechanism

Yan Zhang,YuanBo Bi,JianPing Zhou,DaQian Sun,HongMei Li

DOI: https://doi.org/10.1016/j.matlet.2020.128012

IF: 3

2020-09-01

Materials Letters

Abstract:<p>Laser welding of TC4 Titanium (Ti) alloy to 304 stainless steel (SS) has been applied using Ag45-Cu30-Zn25 alloy as filler metal. A new welding process for SS-Ti alloy joint was introduced on the basis of the controlling the formation of Ti-Fe intermetallics in the joint. One pass welding involving creation of a joint with one fusion weld and one diffusion weld separated by remaining unmelted SS. When laser beam on the SS side was 1.6 mm, SS would not be completely melted in joint. Through heat conduction of unmelted SS, the atomic diffusion occurred at the SS-Ti alloy interface. A diffusion weld was formed at the SS-Ti alloy interface with the main microstructure of AgZn₃+CuZn, α-Cu+Fe₃Zn₂ and Ti₂Cu+TiCu. The joint fractured at the diffusion weld with the maximum tensile strength of 284 MPa.</p>

materials science, multidisciplinary,physics, applied