Abstract:To synergistically improve the strength-ductility of copper alloys used in the miniaturized component, Cu-3.2Ti-0.2Fe-0.2V alloy with heterogeneous structure was obtained by thermo-mechanical treatment (namely, short-time annealing). The heterogeneous structure was composed of the non-uniform grains formed due to Laves phase inhibiting grain growth and FCC structured Cu4Ti phase with good coherent interface precipitated on the grain boundaries in sub-micro size. After aging at 400 °C for 2 h and then 450 °C for 4 h, the ultimate tensile strength and elongation of the heterogeneous-structured alloy were 976.8 MPa and 18.8% respectively, which was approximately 120 MPa more than that of the coarse-grained alloy after complete annealing, but both alloys had comparable ductility. When cold-rolling with 5% reduction was carried out before the aging of 450 °C, the strength increased to 1057 MPa and corresponding elongation was still over 10%. The strengthening mechanism of alloy with heterogeneous structure was analyzed and the hetero-deformation induced hardening of 284.5 MPa was the other significant reinforcement. The semi in-situ observation of tensile deformation behavior shown that the superior ductility in coarse-grained alloy was mainly attributed to the slipping and twinning. While grain rotation and grain boundary sliding were additional deformation mechanism in heterogeneous-structured alloy during tensile deformation, meanwhile, the texture of S, {110}<1 1 ‾ 1> and {331}<1 2 ‾ 3> components converted to the texture of {441}< 1 ‾ 1 ‾ 8>, Goss, Copper and {012}< 8 2 ‾ 1 > components. The deteriorative ductility after rolling with the reduction of 5% was owing to the S and Cube components converted to the strong texture of {032}<22 3 ‾ > components.

Precipitation Behavior and Mechanical Properties of a Novel Cu–2Fe-0.5Ti Alloy Produced by Thermos-Mechanical Treatment

The Evolution of Microstructure and Properties of a Cu–Ti–Cr–Mg–Si Alloy with High Strength During the Multi-Stage Thermomechanical Treatment

Precipitation Behavior and Performance Evolution of Cold-Rolled Cu-Ti-fe Alloy During Heat Treatment

High strength, high conductivity and good softening resistance Cu-Fe-Ti alloy

Microstructure and properties of high strength, high conductivity Cu-2.5Fe-0.3Cr-0.3Mg-0.2Si-0.1Ca-0.1Zr alloy treated by multi-stage thermomechanical treatment

Effects of Fe Content on Properties and Microstructure of Cu–Ti Alloys During Aging

Structural Stability,microstructure and Mechanical Behavior of Ti-10V-2Fe-3Al Alloy

Microstructures and mechanical properties of Cu–Ti alloys with ultrahigh strength and high ductility by thermo-mechanical treatment

Effect of Ti2Cu Precipitates on Mechanical Behavior of Ti–2.5Cu Alloy Subjected to Different Heat Treatments

Metastable Phase Transformations and Mechanical Properties of an As-Extruded TiAl-based Alloy During Two-Step Heat Treatment

Microstructure and Properties of Cu–2.3Fe–0.03P Alloy During Thermomechanical Treatments

Precipitation behavior and microstructural evolution during thermo-mechanical processing of precipitation hardened Cu-Hf based alloys

Suppression of discontinuous precipitation by Fe addition in Cu–Ti alloys

Simultaneously Improved the Strength and Ductility of Cast Al-3Li-2Cu Alloy by Ti Addition and Heat Treatment

Evolutions of the Microstructures and Mechanical Properties of Ti-2.8 Wt%cu Alloy During Heat Treatment

Microstructure and Properties of Cu-10 Wt%fe Alloy Produced by Double Melt Mixed Casting and Multi-Stage Thermomechanical Treatment

Effect of temperature on mechanical behavior of Cu–Cr–Co–Ti alloys

Evolution of Microstructure and Properties of an Ultrahigh Strength Cu-Ni-Sn Alloy with Low Sn Content During the Multi-Stage Thermomechanical Treatment

Thermomechanical treatment of a novel Cu-Zn-Cr alloy and its effect on properties

A Novel Microstructure of Cu-Ti Alloy with Ultrahigh Electrical Conductivity and Strength

Precipitation Behavior and Its Effects on Tensile Properties of Feconicr High-Entropy Alloys