Effects of Carbon-Sequestering Coral Aggregate on Pore Structures and Compressive Strength of Concrete

Renjie Mi,Yifei Wang,Tao Yu,Wengui Li

DOI: https://doi.org/10.1007/s44242-023-00024-4

2023-01-01

Low-carbon Materials and Green Construction

Abstract:CO 2 sequestration/storage shows considerable impacts on the pore structures and compressive strength of concrete. This paper presents a study in which coral aggregates were presoaked in Ca(OH) 2 slurries with different solid-to-liquid ratios (i.e. 0.2, 0.4, and 0.6 g/mL) followed by accelerated carbonation. The effects of CO 2 sequestration on the particle size distribution, cylinder compressive strength, water absorption, and apparent density of coral aggregate were investigated. The evolution of pore structures in coral aggregate concrete after CO 2 sequestration was also studied. Additionally, the effect of CO 2 sequestration on the development of compressive strength of coral aggregate concrete was explored. The results showed that CO 2 sequestration affected the properties of coral aggregate. Moreover, the porosity of CaCO 3 formed by CO 2 sequestration was the highest in the concrete. With the increase of solid-to-liquid ratio, the porosity of cement pastes and the CaCO 3 increased, and more big pores existed in the cement pastes and CaCO 3 . Furthermore, the compressive strength of coral aggregate concrete when the solid-to-liquid ratio was 0.2 g/mL increased compared with that before CO 2 sequestration, but the compressive strength reduced when the ratio increased to 0.6 g/mL.