Abstract:The electrodeposition of a Cu–Sn binary alloy on stainless steel from a cyanide-free alkaline electrolyte containing EDTA·2Na and C4H4O6KNa was investigated to explore the possibility of a cyanide-free double complexing system that maintains the decorative quality and coating performance. The Cu–Sn co-deposition occurred at −0.95 Vvs.Hg|HgO, and the height of cathode peak A from the BR bath was −0.0280 A. EDTA·2Na could simultaneously complex with Cu ions and Sn ions, while C4H4O6KNa could only complex with Cu ions, which was shown through the analysis of the cyclic voltammetry (CV) curves together with the nuclear magnetic resonance (NMR) results. The molar concentration ratio and sum of the two main salts or the two complexing agents, and the pH of the electroplating solutions were shown to influence the surface micromorphology, composition and phase structure of the Cu–Sn coatings. The scanning electron microscopy (SEM) analysis showed that the Cu–Sn coating obtained from the bath with EDTA-tartrate double complexing agents exhibited smaller grain sizes than that obtained from the bath with the single EDTA or tartrate complexing agent, and the smallest grain size of 0.2 μm was obtained from the BR bath. In addition to being smaller than the others, this coating contained uniform particle sizes. The energy-dispersive X-ray spectroscopy (EDS) analysis indicated that the composition of the Cu–Sn coating obtained from the BR bath was 92.8 wt% Cu and 7.2 wt% Sn, and this coating was golden in colour. X-ray diffraction (XRD) showed that the Cu–Sn coatings were crystalline and were composed of a mixture of Cu, Cu6Sn5, [Cu, Sn] and Cu10Sn3 phases, indicating the formation of Cu–Sn binary alloy. These results may provide theoretical guidance for the electrodeposition technology of other alloy coatings.

Study on Composition of Karat Gold Deposition Without Cyanide by Electroforming

Electrochemical Fabrication of Nanoporous Gold

Highlights from Recent Literature

Preparation of cyanide-free gold-tin alloys by ultrasonic-assisted pulse electrodeposition

The study of direct gold electrowinning from dilute cyanide solutions

Technique for Determination of Gold Electrode Area and Its Application of Characterization in Self-Assembling Process

Experimental and theoretical studies of DMH as a complexing agent for a cyanide-free gold electroplating electrolyte

Pulse Electroplating Of Gold-Nickel Alloys: Morphological and Aesthetic Improvement Compared to DC

The electrodeposition of low-Sn imitation gold Cu–Sn alloy from EDTA-tartrate double complexing agents

Copper Deposition on Au(111) in a Deep Eutectic Solvent: An In Situ STM Study**

Uniform Electrochemical Deposition of Copper onto Self-Assembled Gold Nanoparticles

Dynamic Investigation of Cu50at%Au (001) Alloy Film Nano-oxidation by in Situ UHV TEM

Computational Chemistry and Electrochemical Studies of Adsorption Behavior of Organic Additives during Gold Deposition in Cyanide-free Electrolytes

Effects of four carboxyl-containing additives on imitation gold electroplating Cu-Zn-Sn alloys in an HEDP system

Electrochemical deposition and stripping of copper, nickel and copper nickel alloy thin films at a polycrystalline gold surface: a combined voltammetry-coulometry-electrochemical quartz crystal microgravimetry study

Copper Metallization of Gold Nanostructure Activated Polypyrrole by Electroless Deposition

Resistance to Electrical Corrosion of Au-Cu Alloy Coatings for Electronic Contacts

Electrochemical analysis of copper-EDTA-ammonia-gold thiosulfate dissolution system

Anodic Behaviour of Gold in Cyanide Solution

Electrochemical dissolution behavior of gold and its main coexistent sulfide minerals in acid thiocyanate solutions

Study on the preparation mechanism and property analysis of a localized Au coating by laser-induced cyanide-free electroplating