Abstract:In this study, Titanium (IV) Oxide (TiO2) microspheres were synthesized by hydrothermal method, and Cerium Oxide (CeO2) nanoparticles in the ratios of 0.1, 0.25, 0.5 and 1 mol% were loaded onto these microparticles by surfactant-assisted (Pluronic 123) sol–gel method. The crystal properties and surface morphology of the synthesized TiO2–CeO2 hybrid photocatalysts were investigated by X-ray diffraction method (XRD) and field emission scanning electron microscope (FESEM). Bond structures and surface areas were examined by Fourier-transform infrared spectroscopy (FTIR), Raman and Brunauer–Emmett–Teller (BET) analysis, respectively. XRD patterns with (101) and (200) main planes show that nanoparticles have anatase TiO2 phase. Also, A1g, B1g and Eg Raman modes confirms anatase TiO2 phase. In addition, with CeO2 doping, while the average crystallite size of nanoparticles decreased, their surface area increased. The photocatalytic activity of the prepared photocatalysts were investigated by degradation of the methylene blue (MB) under UV light (λ = 365 nm). The results showed that the surface area and crystal structure of hybrid structure and interface interaction between TiO2 and CeO2 have a significant effect on photocatalytic performance. The 0.1% CeO2–TiO2 photocatalyst degraded almost 95% of the MB solution in about 60 min, while for TiO2 microspheres this value is around 80%. Also, we observed that 0.1% CeO2–TiO2 led to about 1.4 times higher reaction rate in comparison to TiO2. Results showed that the hybrid photocatalysts has a higher performance than bare TiO2 microspheres.

Preparation and Photocatalytic Properties of TiO_2@SiO_2 Microspheres

Preparation of TiO_2/SiO_2 and Photo-Catalytic Degradation of Methyl-Orange

Preparation and Photocatalytic Properties of TiO_2 Microspheres

Microorganism-Templated Nanoarchitectonics of Hollow TiO2-SiO2 Microspheres with Enhanced Photocatalytic Activity for Degradation of Methyl Orange

Preparation of SiO2@Au@TiO2 Core–shell Nanostructures and Their Photocatalytic Activities under Visible Light Irradiation

Preparation and Characterization of SiO<SUB>2</SUB>/TiO<SUB>2</SUB>-Pt Core/Shell Nanostructures and Evaluation of Their Photocatalytic Activity

Preparation,Characterization and Photocatalytic Activity of Three-dimensionally Ordered Mesoporous/Macroporous TiO2 Microspheres

Studies on Preparation and Characterization of 3DOM TiO2 and TiO2/SiO2 Materials with High Photocatalytic Ability

Synthesis of Highly Monodispersed Teardrop-Shaped Core–shell SiO2/TiO2 Nanoparticles and Their Photocatalytic Activities

A Simple Solvothermal Process to Synthesize CaTiO3 Microspheres and Its Photocatalytic Properties

Porous TiO2 Hollow Nanospheres: Synthesis, Characterization and Enhanced Photocatalytic Properties

Synthesis and Photocatalytic Property of SiO2/TiO2

Preparation of Hollow TiO2 Microspheres Using a Novel Polymer Microsphere Template

Preparation of TiO2 Composite Photocatalyst Using Amorphous SiO2 Microspheres Loaded with Spent SCR Catalysts

Template-Free Fabrication of Rattle-Type Tio2 Hollow Microspheres with Superior Photocatalytic Performance

A new approach to optimize the synthesis parameters of TiO2 microsphere and development of photocatalytic performance

Edta-Assisted Fabrication Of Tio2 Core Shell Microspheres With Improved Photocatalytic Performance

Facile flame thermal synthesis of SiOx-C/ TiO2 microspheres with enhanced photocatalytic performance

Preparation and Characterization of Nano TiO2/SiO2 Catalyst

Preparation of Multilayered Core-Shell TiO2@DR@SiO2 Composites and Investigation of Its Photocatalytic Performance

Synthesis and Photocatalytic Property of TiO<sub>2</sub> Particles Preparated in the Solvothermal Method