Effects of Thermal Aging on Corrosion Resistance of Duplex Stainless Steel Fabricated by Different Methods
Hillane Mirelle Lopes Ferreira de Lima,Antônio Mateus de Carvalho Costa,Maria Sthefane de Oliveira Matos,Sérgio Souto Maior Tavares
DOI: https://doi.org/10.1007/s11665-024-10227-w
IF: 2.3
2024-10-09
Journal of Materials Engineering and Performance
Abstract:Two duplex stainless steels UNS32205 previously submitted to aging thermal treatment at 475 °C, were characterized by electrochemical tests in an aqueous 0.6 mol/L NaCl solution. The results were discussed, taking into consideration the effects of microstructural modifications caused by the aging at 475 °C, as well as the impact of two important fabrication routes for many applications of this steel, namely, hot rolling and powder metallurgy with hot isostatic pressing on the corrosion resistance of the materials. Heat treatment at 475 °C causes the spinodal decomposition of the ferrite phase, resulting in a chromium-rich phase, α ', and an iron-rich phase, α . The influence of alpha line phase ( α ') on the corrosion resistance of duplex stainless steels is well known; however, few studies in the literature compare how the microstructure obtained with these fabrication routes can affect the embrittlement at 475 °C of these steels. The results showed that the production of these alloys through powder metallurgy with hot isostatic pressing (HIP) delayed the embrittlement of steel at 475 °C, as the steel obtained by HIP exhibited better corrosion resistance under the condition of aging at 475 °C for 40 hours.
materials science, multidisciplinary