Synthesis of Hyperbranched Poly(ester amide)s and Their Application in Polycarbonate as Rheological Modification Agent
Yu-ling Wang,Wu-song Li,Cong-cong Liu,Wei Huang,De-yue Yan,Hong-qiang Kang
DOI: https://doi.org/10.11777/j.issn1000-3304.2017.16355
2017-01-01
Acta Polymerica Sinica
Abstract:Due to highly branched three-dimensional sphere-like molecular architecture, hyperbranched polymers have shown very different properties such as intramolecular cavities, low viscosity, high solubility and a large number of terminal functional groups if compared with their linear analogues. They can be facilely synthesized via a one-pot polymerization through different methods according to the type of monomers, including polycondensation of AB(n) monomers, self-condensing vinyl polymerization, self-condensing ring-opening polymerization and so on. Here, hyperbranched poly(ester amide)s (HBPEAs) with terminal carboxyl groups are prepared from benzene-1,2,4-tricarbonylic acid-1,2-anhydride (BTAA) and ethanolamine (EMA) via two-step and one-step melt polycondensation, respectively. In two-step method, the anhydride group in BTAA first reacted with the amino group in EMA to form a AB(2) intermediate with one hydroxyl groups and two carboxyl groups in ethanol according to the principle of non-equal reactivity of functional groups. After ethanol evaporated, the AB(2) intermediate was melted at 220 degrees C to polymerize to produce HBPEA without gelation. Furthermore, HBPEA was also synthesized from BTAA and EMA at 220 degrees C through one-step melt polycondensation, more convenient in the industry. The resulting HBPEAs were characterized by H-1-NMR analysis, Ubbelohde viscometer, differential scanning calorimeter (DSC), thermo gravimetric analyzer (TGA) and refractive index measurements. their DBs are about 0.64 and intrinsic viscosities are about 0.120 similar to 0.146 dL/g. Their T(g)s are about 125 degrees C and refraction indexes are about 1.57 similar to 1.58, which is similar to those of PC. The temperature of 5 wt% weight loss is above 350 degrees C. Therefore, HBPEAs can be used as modification agent to process polycarbonate. When HBPEAs were added into PC or PC/CaCO3, not only the process ability of PC or PC/CaCO3 was improved, but also the colour of PC was kept unchanged. In addition, the mechanical properties and the surface roughness of PC or PC/CaCO3 were enhanced too. In summary, HBPEAs have very broad prospects for different applications.