Synthesis of a Novel Phosphorus-Containing Polymer and Its Application in Amino Intumescent Fire Resistant Coating

Guojian Wang,Yan Huang,Xiang Hu

DOI: https://doi.org/10.1016/j.porgcoat.2012.09.005

IF: 6.6

2013-01-01

Progress in Organic Coatings

Abstract:A mixture (denoted as PX) of phosphates was prepared by the reaction of phosphoric acid and a kind of bicyclic pentaerythritol phosphate (PEPA, 1-oxo-1-phospha-2,6,7-trioxabicyclo[2.2.2]-4-hydroxymethyl octane). Then PX was successfully copolymerized with PEG200 to achieve a novel phosphorus-containing polymer (denoted as PX-co-PEG). 31P NMR, 1H NMR and FT-IR analysis results showed that there were 38.7 wt.% PEPA phosphates and 61.3 wt.% pentaerythritol biphosphates in the PX mixture. The result of GPC indicated that the molecular formula of PX-co-PEG could be noted as PX2.0PEG3.0. Fire protection test results proved that PX-co-PEG modified amino resin applied on the plywood boards effectively extended the protection time over flame. The decomposition process of fire resistant coating was studied by thermogravimetric analysis and FT-IR which could be divided into three characteristic temperature stages. The solid residue was kept to be 14.6 wt.% at 787 °C.