Abstract:A phosphorus-nitrogen flame retardant curing agent (named as PPMXD ) was synthesized from phenylphosphonic dichloride (PPDC ) with m-xylylenediamine (MXDA ) and characterized by FTIR,1 HNMR,ESI-MS. Its thermal stability was tested by TGA and DSC. Some factors affecting the yield of PPMXD such as mole ratio of reactants,solvent type and proportion,reaction temperature and time were investigated. The results demonstrated that the optimum conditions for synthesis of PPMXD were as follows:the reaction temperature was 20 ℃,the reaction time was 7 hours,the mole ratio of PPDC to MXDA was 1. 0:3. 5,the mixture of N,N dimethylformamide (DMF)and methylene chloride with a volume ratio of 1:17 was used as a solvent,the mass ratio of solvent to PPDC was 12:1. Subsequently,PPMXD was applied in epoxy resin (E-51 ),and the flame retardancy of the resulting composite material was determined by limiting oxygen index (LOI)measurements and vertical (UL-94)tests. The thermal stability and carbon residue morphology of the epoxy resin were characterized by TGA and SEM. Sample EP2 containing 40% PPMXD (based on the mass of the E-51 )could achieve UL-94 V-0 rating with a LOI value of 29 . 0%,and the tensile strength and impact strength could reach 42. 89 MPa and 6. 45 kJ/m2 ,respectively. TGA indicated that the addition of PPMXD could reduce the largest thermal decomposition rate of EP2 (12. 73%/min ) compared with that of E-51 (18. 23%/min). Meanwhile,sample EP2 had a relatively high char yield (18. 86% at 800 ℃),higher than that of E-51 (16. 12%). SEM results showed that the surface of char residue was rough consisting of obvious foams,which indicated that PPMXD performed good flame retardancy for epoxy resin.

Synthesis of Phosphorus-nitrogen Flame Retardant Curing Agent and Its Effect on Performance of Epoxy Resin