Syntheses of Two Dopo-Based Reactive Additives As Flame Retardants and Co-Curing Agents for Epoxy Resins
Xiao Ling,Dechao Sun,Tian-li Niu,Youwei Yao
DOI: https://doi.org/10.1080/10426507.2014.884092
2014-01-01
Abstract:GRAPHICAL ABSTRACT Abstract Two novel phosphorus-nitrogen-containing flame retardants, 1,1′,2,2′-tetra-hydroxyl-4′′, 4′′′-biphenylene-bis[amino-((10′′′′-O-10′′′′-H-9′′′′-oxa-10′′′′λ5-phosphaphenanthrene-10′′′′-yl))-methyl]}-bisphenol (3) and 1,1′,2,2′-tetra-hydroxyl-{4′′,4′′′-phenylene-bis[amino-((10′′′′- O-10′′′′- H-9′′′′- oxa-10′′′′λ5-phosphaphenanthrene-10′′′′-yl))-methyl]}-bis-phenol (4) were synthesized by two steps: 1,1′,2,2′-tetra-hydroxyl-{4′′,4′′′- bi-phenylene-bis[amino-methyl]}-bis-phenol, imine (1), was synthesized through condensation reaction between 3,4-dihydroxybenzaldehyde and 4,4′-diaminobiphenyl; and, 1,1′,2,2′-tetra-hydroxyl-{4′′,4′′′- phenylene-bis[amino-methyl]}-bis-phenol, imine (2) was synthesized by the reaction of 3,4-dihydroxybenzaldehyde and 1,4-phenylenediamine; then, addition reactions between 9,10-dihydro-9-oxa-10- phosphaphenanthrene-10-oxide and the two imines, the (3) and (4) were obtained, respectively. (1)–(4) were characterized by FTIR, NMR, and MS. (3) and (4) reacted with epoxy resins as co-curing agents with 4,4′-diaminodiphenylmethane. Compared with control samples, (3) or (4) co-cured epoxy thermosets with phosphorus content of 1.0 wt% possessed good flame retardant properties with LOI value reaching more than 36.0, higher char yields. The glass translation temperature (Tg) of thermosets containing (3) or (4) were characterized with suitable changes by DSC test.