Abstract:In this study, the mechanical behaviors of nano-SiO2 reinforced geopolymer concrete (NS-GPC) under the coupling effect of a wet–thermal and chloride salt environment were investigated through a series of basic experiments, and a simulation on the coupling effect of a wet–thermal and chloride salt environment and SEM test were also included. During the experiments for the coupling effect of the wet–thermal and chloride salt environment, an environment simulation test chamber was utilized to simulate the wet–thermal and chloride salt environment, in which the parameters of relative humidity, temperature, mass fraction of NaCl solution and action time were set as 100%, 45 °C, 5% and 60 d, respectively. The content of nano-SiO2 (NS) particles added in geopolymer concrete (GPC) were 0, 0.5%, 1.0%, 1.5% and 2.0%. The result indicated that the mechanical properties of NS reinforced GPC decreased under the coupling effect of the wet–thermal and chloride salt environment compared to the control group in the natural environment. When the NS content was 1.5%, the cube and splitting tensile strength, elastic modulus and impact toughness of GPC under the coupling environment of wet–thermal and chloride salt were decreased by 9.7%, 9.8%, 19.2% and 44.4%, respectively, relative to that of the GPC under the natural environment. The addition of NS improved the mechanical properties of GPC under the coupling effect of the wet–thermal and chloride salt environment. Compared to the control group without NS, the maximum increment in cube compressive strength, splitting tensile strength and elastic modulus of NS–GPC under the coupling effect of the wet–thermal and chloride salt environment due to the incorporation of NS reached 25.8%, 9.6% and 17.2%, respectively. Specifically, 1.5% content of NS increased the impact toughness, impact numbers of initial crack and the ultimate failure of GPC by 122.3%, 109% and 109.5%, respectively.

Reactive Powder Concrete Reinforced with Nano SiO2-coated TiO2

The Mechanical and Self-Sensing Performance of Reactive Powder Cement Concrete with Nano-Stainless Steel Powder

Study on the reinforcing mechanisms of nano silica to cement-based materials with theoretical calculation and experimental evidence

Enhanced early hydration and mechanical properties of cement-based materials with recycled concrete powder modified by nano-silica

Effect of nano-silica as cementitious materials-reducing admixtures on the workability, mechanical properties and durability of concrete

Performance and microscopic study of various mineral admixtures on reactive powder concrete

Synthesis of Nano-Sio2@ptpeg-vpa Copolymer and Its Effects on Early-Age Cement Hydration

Flow Mechanism and Strength Characteristics of Textile Reinforced Concrete Mixed with Colloidal Nano-SiO2

Bending Toughness and Calculation Model of Ultrahigh-Performance Concrete with Hybrid Micro- and Nanofillers

Systematic investigation into mechanical strength, pore structure and microstructure of high performance concrete incorporating nano-hybrids

Influence of Nano-SiO2 Content on Cement Paste and the Interfacial Transition Zone

Effect of Different Particle Sizes of Nano-Sio2 on the Properties and Microstructure of Cement Paste

Comparative study of nanomaterials activated recycled powders from demolition and decoration wastes as supplementary cementitious material

Investigating pore structure of nano-engineered concrete with low-field nuclear magnetic resonance

Insights on the influence of nano-Titanium dioxide and nano-Zinc oxide on mechanical properties and inhibiting of steel reinforcement

Investigation on the Properties of Sustainable Steel Fiber Reinforced Reactive Powder Concrete by Utilization of Coir Pith Aggregates and Pyrogenic Silica

Reinforcement of Cement Nanocomposites through Optimization of Mixing Ratio between Carbon Nanotube and Polymer Dispersing Agent

Incorporating Nano-Silica (NS) into Concrete Mixtures

Surface treatment with nano-silica and magnesium potassium phosphate cement co-action for enhancing recycled aggregate concrete

Mechanical Properties of Nano-SiO2 Reinforced Geopolymer Concrete under the Coupling Effect of a Wet–Thermal and Chloride Salt Environment