Green and red luminescence in Tb³⁺and Eu³⁺:Zn 2 SiO 4 powders

S. Buddhudu,Hong Xi Zhang,C. H. Kam,Seng Lee Ng,Boon S. Ooi,Yee Loy Lam,Yuen Chuen Chan,Yan Zhou,Wenxiu Que,Terence Kin Shun Wong

DOI: https://doi.org/10.1117/12.382881

2000-01-01

Abstract:We report the preparation and photoluminescence spectral analysis of Tb<SUP>3+</SUP> and Eu<SUP>3+</SUP> doped Zn<SUB>2</SUB>SiO<SUB>4</SUB> powders in sol-gel sol-gel process. On exposure to an UV source, these rare earth ions doped zinc silicate materials have shown prominent luminescent green and red colors, due to the electronic transitions of <SUP>5</SUP>D<SUB>4</SUB> yields <SUP>7</SUP>F<SUB>5</SUB> (Tb<SUP>3+</SUP>) and <SUP>5</SUP>D<SUB>0</SUB> yields <SUP>7</SUP>F<SUB>2</SUB> (Eu<SUP>3+</SUP>) respectively. The green emitting transition of Tb<SUP>3+</SUP> material has been a magnetic dipole in nature and the red emitting transition of Eu<SUP>3+</SUP> material has been due to an electric dipole in nature with a hypersensitivity in its luminescence. Systematic characterization has been carried out to understand the fluorescence efficiency of these two materials by measuring their excitation, photoluminescence, time-resolved luminescence spectra and lifetimes of the emission transitions (<SUP>5</SUP>D<SUB>0</SUB> yields <SUP>7</SUP>F<SUB>0,1,2,3,4&5</SUB>) of Eu<SUP>3+</SUP> at two different excitation wavelengths of 226 nm and 395 nm. However, for the emission transitions (<SUP>5</SUP>D<SUB>4</SUB> yields <SUP>7</SUP>F<SUB>6,5,4,3,2&1</SUB>) of Tb<SUP>3+</SUP> doped material, one excitation wavelength of 229 nm was used. Structural characteristics of these materials was carried out with an XRD and TEM measurements. The computed color coordinates suggest that both the phosphors have all desirable features for CRT screen applications.