Abstract:Flames propagating along the sample edges (edge flame) will transform two-dimensional flame spread into three-dimensional flame spread, causing a significant interference with results of material flammability test. A potential method to minimize above effect is utilizing an inert wall to inhibit the side surface of sample with a designed air gap distance. In this work, the downward flame spread along the sample edge with various air gap distances is systematically studied. Cast PMMA with thicknesses from 0.4 to 2.5 mm were used as samples. The general trend of flame spread rate (FSR) at edge with respect to air gap distance can be summarized into three regimes: when the air gap distance is less than 2 mm, the edge flame is quenched by wall heat loss, and the overall flame spread behavior is two-dimensional. Then, the edge flame appears after the air gap distance exceeds 2 mm, resulting in a sharp increase in FSR. This critical air gap distance for the onset of edge flame is less sensitive to the sample thickness. Finally, as the air gap distance continues to increase, the FSR gradually approaches the asymptotic value of the uninhibited sample. With the increase in air gap distance, thermally-thin assumption loses validity as a result of the reduction in residence time of solid phase (larger FSR). To interpret the general trend of FSR with respect to air gap distance, a modified flame spread model based on conventional thermal theory is developed. The effect of air gap distance on flame spread along sample edge is characterized by two correction factors, one of which describes solid surface curvature at sample edge, the other of which is the effective flame temperature considering the heat loss from the spreading flame to the metal wall. The new model well reproduces the experimental results, and further supports the significance of heat loss in the trend of flame spread rate. This work helps to understand the flame spread mechanism under effects of solid surface curvature and heat loss, while also providing scientific support for optimization of material flammability testing standards.

A Criterion of Dimensional Design to Improve Flame Spread Resistance of Magnesium Alloy Components

Flame Ignition Mechanism of Magnesium Alloys Controlled by Oxide Films Based on the Oxidation Behaviors of Al, Nd and Y

Combustion of Mechanically Alloyed Al∙Mg Powders in Products of a Hydrocarbon Flame

Effects of Al, Zn, and rare earth elements on flammability of magnesium alloys subjected to sonic burner–generated flame by Federal Aviation Administration standards

Flame resistance and oxidation behaviour of Mg–xCa (x=0.3, 1.0, 2.0 and 3.6 wt.%) alloys

Flame Propagation Behaviours and Explosion Characteristics of Al Mg Alloy Dust Based on Thermodynamic Analysis

Flame propagation behaviours and explosion characteristics of AlMg alloy dust based on thermodynamic analysis

Fire Spread over Charring Materials: Influence of the Sample Orientation and External Radiant Intensity

Sample Width and Thickness Effects on Upward Flame Spread over PMMA Surface.

Flame propagation behaviors and temperature distribution characteristics of magnesium dust clouds with different particle size polydispersities

Recent Advances on the Oxide Film of Ignition-Proof Magnesium Alloys: A Review

Research Progress on the Oxidation Behavior of Ignition-Proof Magnesium Alloy and Its Effect on Flame Retardancy with Multi-Element Rare Earth Additions: A Review

Oxidation Resistance of Mg-Xca (X=0.3, 1.0, 2.0 and 3.6 Wt.%) Alloys in Flame

Investigation into the Mechanism of Ignition of Magnesium Alloy Plates by High-Temperature Molten Droplet

Influence of Flame Rectification on Mechanical Properties of AlZnMg Alloy

Post-fire residual service performance of magnesium alloys reinforced by rare earths

Study on laser ignition and combustion characteristics of micron-sized aluminum and Al-Mg alloys particles

Effect of solid surface curvature and wall heat loss on the downward flame spread along the edge of thin PMMA sheets

Ignition-proof Properties of a High-Strength Mg-Gd-Ag-Zr Alloy

Hazard evaluation, explosion risk, and thermal behaviour of magnesium- aluminium alloys during the polishing process by using a 20-L apparatus, MIEA, and TGA

Research and Development of New Style Ignition-proof Magnesium Alloys