Effect of Al 2 O 3 and MgO on crystallization and structure of CaO–SiO 2 –B 2 O 3 -based fluorine-free mold flux

Jun-yu Chen,Wan-lin Wang,Le-jun Zhou,Zi-hang Pan

DOI: https://doi.org/10.1007/s42243-020-00439-4

2020-01-01

Journal of Iron and Steel Research International

Abstract:The crystallization behavior and melt structure of the CaO–SiO 2 –B 2 O 3 -based fluorine-free mold flux were investigated. The results show that the crystallization of the mold flux was first inhibited and then promoted with the increase in Al 2 O 3 content from 4 to 12 wt.%. However, it was enhanced by MgO in the range of 2–10 wt.%. The results of Fourier transform infrared spectroscopy and Raman spectroscopy showed that Al 2 O 3 worked as a network former in the mold flux melt when its content was in the range of 4–8 wt.%, whereas it worked as the network breaker to provide O 2− when its content was in the range of 8–12 wt.%. In addition, the combined effects from the charge compensation by Mg 2+ and the network broken by O 2− led to the increase in some typical T–O–T (Al–O–Al, B–O–B, etc.) and simpler structural units (Q 0 (Si), B–O − in the [BO 2 O − ], etc.) when the MgO content was in the range of 2–6 wt.%. The continuous increase in O 2− provided by the addition of MgO from 6 to 10 wt.% further depolymerized the network of the melt and finally caused fast crystallization.