Effect of Surface Crosslinking on the Wear and Friction Behavior of Tea Polyphenol Stabilized Ultra-High Molecular Weight Polyethylene for Total Joint Replacements
Adnan Ahmad,Nouman Ali Shah,Rizwan M. Gul,M. Ali Kamran,M. Aaqib Ishaq,Jia Zhuang Xu,Zhong Ming Li,Binnur Sagbas
DOI: https://doi.org/10.21203/rs.3.rs-4341120/v1
2024-01-01
Abstract:Abstract Highly crosslinked ultra-high molecular weight polyethylene (UHMWPE) with vitamin E (VE) as an antioxidant is widely accepted as a bearing material for joint implants. VE significantly helps in resisting oxidation, but it poses concerns about the loss of crosslink density and causes deterioration of the wear performance. This research aims to hypothesized that tea polyphenols, such as lipid-soluble epigallocatechin gallate (lsEGCG) and epigallocatechin gallate (EGCG) could inhibit the usual decrease in crosslink density due to VE, leading to higher wear performance. The antioxidants were blended with UHMWPE at 0.2 wt%, followed by surface chemical crosslinking using di-cumyl peroxide. The surface properties such as crosslink density, roughness, co-efficient of friction and wear performance is evaluated in detail. The results show a significantly higher crosslinked density of lsEGCG and EGCG blended UHMWPE, compared to VE stabilized UHMWPE, which was 17% lower than the virgin UHMWPE. The co-efficient of friction increased after crosslinking and was relatively higher in tea polyphenol blended UHMWPE, confirming a highly crosslinked network structure. The wear resistance of surface crosslinked tea polyphenol stabilized UHMWPE was significantly higher in comparison to crosslinked UHMWPE stabilized with VE. In addition, a substantial number of scratches, furrows, and flakes were observed on the surface of VE stabilized UHMWPE as compared to tea polyphenol stabilized UHMWPE. It was concluded that tea polyphenols are promising alternatives to VE for improvement in the overall performance and longevity of UHMWPE based implants.