Leaching stability of simulated waste forms for immobilizing An 3+ by Gd 2 Zr 2 O 7 with Nd 3+

Xirui Lu,Mengjun Chen,Faqin Dong,Xiaoli Wang,Yanlin Wu,Zhengxue Xiao

DOI: https://doi.org/10.1007/s11595-014-1014-4

2014-01-01

Journal of Wuhan University of Technology-Mater. Sci. Ed.

Abstract:In order to investigate the anti-leaching capability of pyrochlore Gd 2 Zr 2 O 7 immobilized An 3+ , trivalent neodymium was used as the simulacrums for radioactive wastes with trivalence, Gd 2− x Nd x Zr 2 O 7 (0.0⩽ x ⩽2.0) series samples were successfully synthesized by high temperature solid reaction and using Gd 2 O 3 , ZrO 2 powders as starting materials. The experiments of long-term chemical stability were conducted in synthetic seawater at 40 and 70 °C. The XRD diffractive data and extraction ratio of as-received samples were collected with the help of X-ray diffraction (XRD) instrument and inductively coupled plasma mass spectrometry (ICP-Mass). The results indicate that the phases of as-received compounds keep the single phase of pyrochlore. The extraction ratio of Gd 3+ , Zr 4+ and Nd 3+ in waste forms is increasing with the increase of immersion time in synthetic seawater. The extraction ratio of waste forms at 70 °C is higher than at 40 °C. The highest extraction ratio of Gd 3+ , Zr 4+ and Nd 3+ after 42 days is near 0.025 8, 0.003 8 and 0.045 2 μg·mL −1 , respectively.