Synthesis and Structural Transformations of (Gd1-Xcex)(2)zr2o7+x: an Analogue for Pu Immobilization

Zhao Pei-Zhu,Li Lin-Yan,Xu Sheng-Ming,Zhang Qin

DOI: https://doi.org/10.3866/pku.whxb201304013

2013-01-01

Abstract:Gd2Zr2O7 is a well known host for nuclear waste immobilization because of the high neutron absorption cross section of Gd and low energy transformation between ordered pyrochlore and disordered defect-fluorite structures. Pyrochlore Gd2Zr2O7 was synthesized at relatively low temperature (compared with traditional high temperature solid-state reaction) using Gd(NO3)(3)center dot nH(2)O, Zr(NO3)(4)center dot nH(2)O as a starting material and a small amount of NaF as fluxing agent. Ce4+ was used as an analogue for Pu4+ and its immobilization behavior in Gd2Zr2O7 was studied in a series of solidified forms comprising (Gd1-xCex)(2)Zr2O7+x (0 <= x <= 0.6). Powder X-ray diffraction (XRD) data showed that the sample structure transformed from pyrochlore to defect-fluorite type with increasing x but maintained constant unit cell volumes. As x was increased to 0.6, the diffraction peaks showed broadening, suggesting considerable lattice distortion. When x= 1, i.e., all Gd3+ was placed by Ce4+, the product was not Ce2Zr2O8, but a phase separated mixture of tetragonal (Zr0.88Ce0.12)O-2 and an ideal fluorite (Ce0.75Zr0.25)O-2. Leach rate measurements indicated that the leach rate of Gd3+, Zr4+, Ce4+ was low when x <= 0.2, but increased significantly when x >= 0.4. This suggests that the substitution rate of Pu4+ for Gd3+ should not be more than 40% when Gd2Zr2O7 is used as the host matrix for Pu4+.