Study on Corrosion Resistance of Zr-702 Zirconium Plate TIG Welded Joint in Sulfuric Acid Environment

Li Ning,Zhang Min,Niu Jing,Yei Jianlin

2022-01-01

Rare Metal Materials and Engineering

Abstract:Tungsten-argon arc welding (TIG) of Zr-702 zirconium plate was carried out with 99.999% high purity Ar as shielding gas and the corrosion resistance of Zr-702 welded joint immersed in 15wt% sulfuric acid at 250 degrees C for 2 and 180 d was studied by static isothermal mass loss method. The results show that the corrosion rate of the welded joint is higher than that of the base metal in the immersion test for different time. When soaking for 2 d, both the welding joint and the base metal have good corrosion resistance. The corrosion resistance of welded joints deteriorates when the soaking time is extended to 180 d, and the corrosion rate of welded joints is greatly affected by the soaking time. Further analysis results show that the corrosion of base metal in sulfuric acid medium is mainly uniform. For welded joints, a large amount of zirconium hydride is precipitated in the weld zone and heat-affected zone, showing the characteristics of hydrogen corrosion. At the same time, the welded joint exhibits remarkable gradient structure and potential difference, so its corrosion is local corrosion combined with galvanic corrosion and hydrogen corrosion.