Regulation of Surface Micro-Nano Structure of Porous Fe-Mn Alloy and Evaluation on Its Biological Performance

Chen Zhikun,Yuan Bo,Nie Yong,Peng Huabei,Zhu Xiangdong,Zhang Xingdong

2022-01-01

Rare Metal Materials and Engineering

Abstract:Fe-based biodegradable metals having good biocompatibility and excellent mechanical property exhibit great promise for applications in orthopedic implants, while the slow degradation rate is a major bottleneck. In this study, the surface of the porous Fe-30Mn scaffold was dealloyed by electrochemical technology. When using hydrochloric acid and sodium chloride as medium solution in dealloying treatment, micro-nano porous network and sheet-like structures were formed on the surface of the scaffolds, respectively. The contact angle and surface roughness tests show that the two micro-nano structure significantly improves the hydrophilicity of the Fe-30Mn scaffold and enhances its roughness. The Fe-30Mn with micro-nano porous network exhibits higher roughness and hydrophlicity than that of the Fe-30Mn with sheet-like structures. The degradation rate of the scaffolds before and after alloying were evaluated by the static immersion method and electrochemical corrosion test. The results show that the construction of surface micro-nano structure can accelerate the degradation of the scaffold. The in vitro cell culture using MC3T3-E1 cells shows that all porous Fe-30Mn scaffolds has good cytocompatibility. The above results confirm that the Fe-30Mn scaffold has a suitable degradation rate and good biocompatibility after electrochemical dealloying treatment, suggesting its great clinical application prospect in the fields of bone repair.