Abstract:Using a solvent-free radical grafting technique, glycidyl methacrylate (GMA) and maleic anhydride (MAH) were used as functionalized graft monomers, styrene (St) as a copolymer monomer, and grafted onto polylactic acid (PLA). A series of PLA-g-(GMA/MAH-co-St) graft copolymers were prepared by adjusting the GMA/MAH ratio. Subsequently, the prepared graft copolymers were used as a compatibilizer with PLA and polypropylene carbonate (PPC) for melt blending to prepare PLA/PPC/PLA-g-(GMA/MAH-co-St) blends. The effects of changes in the GMA/MAH ratio in the graft copolymer on the thermodynamics, rheology, optics, degradation performance, mechanical properties, and microstructure of the blend were studied. The results found that GMA, MAH, and St were successfully grafted onto PLA, and the PLA-g-(GMA/MAH-co-St) graft copolymer obtained from the reaction had a good toughening effect on the PLA/PPC blend system, which significantly improved the mechanical properties of the PLA/PPC/PLA-g-(GMA/MAH-co-St) blend without reducing its degradation performance, resulting in a biodegradable blend material with excellent comprehensive performance. In the PLA-g-(GMA/MAH-co-St) grafting reaction system, when GMA/MAH = 1.5/1.5 (w/w), the grafting degree of the graft copolymer increased most significantly, from 0.83 phr to 1.51 phr. This composition of graft copolymer can effectively improve the compatibility between PLA and PPC. The resulting PLA/PPC blend can maintain good melt flow properties (MFR of 14.51 g/10 min), high transparency, and low haze (light transmittance of 91.56 %, haze of 20.5 %), while significantly improving its thermal stability (T95%, Tmax, and Et increased by 12.87 °C, 20.33 °C, and 32.00 kJ/mol, respectively). Moreover, when introducing PLA-g-(GMA/MAH-co-St) (GMA/MAH = 1.5/1.5 (wt/wt)) graft copolymer into the system, the toughness of the PLA/PPC/PLA-g-(GMA/MAH-co-St) blend system is optimal, with the notch impact strength and fracture elongation increasing to 184.6 % and 535.4 % of the PLA/PPC blend, respectively, at which point the fracture surface of the impact sample shows a wrinkled fracture feature indicative of toughness.

Synergistic Effect of GMA and TMPTA As Co-Agent to Adjust the Branching Structure of PLLA During UV-induced Reactive Extrusion

Blending Effects on Polymorphic Crystallization of Poly(l-lactide)

Poly(L-Lactide) Materials with Balanced Mechanical Properties Prepared by Blending with Peg-Mb-Ppa Multiblock Copolymers

Competing Stereocomplexation and Homocrystallization of Poly(l-lactic Acid)/poly(d-Lactic Acid) Racemic Mixture: Effects of Miscible Blending with Other Polymers

Tuning the Rheological, Thermal, and Solid-State Properties of Branched PLA by Free-Radical-Mediated Reactive Extrusion

Improvement of rheology and mechanical properties of PLA/PBS blends by in-situ UV-induced reactive extrusion

Preparation and Characterization of High-Melt-Strength Polylactide with Long-Chain Branched Structure Through Γ-Radiation-induced Chemical Reactions

Improvement of PLLA Ductility by Blending with PVDF: Localization of Compatibilizers at Interface and Its Glycidyl Methacrylate Content Dependency

Preparation of high melt strength polypropylene by the reactive extrusion process and its foaming application

Effect of Ethylene/butyl methacrylate/Glycidyl Methacrylate Terpolymer on toughness and biodegradation of poly (l-lactic acid)

Melt synthesis and characterization of poly(L-lactic acid) chain linked by multifunctional epoxy compound

High Melt Performance Poly (lactic acid) with Dual Hybrid Long Branching Chains Prepared by Chain Degradation and Restructuring

High performance branched poly(lactide) induced by reactive extrusion with low-content cyclic organic peroxide and multifunctional acrylate coagents

Designing of reactive micro-crosslinked PBAT as the efficient biodegradable toughener for PLLA

Long chain branching polylactide: Structures and properties

High-performance and functional fully bio-based polylactic acid/polypropylene carbonate blends by in situ multistep reaction-induced interfacial control

Enhancement of the properties of biodegradable poly(L-lactide)/poly(butylene carbonate) blends by introducing stereocomplex polylactide crystals

Star Shaped Long Chain Branched Poly (lactic Acid) Prepared by Melt Transesterification with Trimethylolpropane Triacrylate and Nano-ZnO

Enhancing Crystallization Behavior for Optimized Performances of Poly(tmc‐b‐(lla‐ran‐ga)) by PDLA/PLLA Stereocomplex Crystallization

Relationship between the Stereocomplex Crystallization Behavior and Mechanical Properties of PLLA/PDLA Blends

Preparation and characterization of long‐chain branched PA6 by UV‐irradiation of included methacrylate monomers after extrusion