Mechanical Properties of (LaxYb1-x)(2)Zr2O7 Thermal Barrier Coatings

Wang Min,Lai Xinchun,Yang Jun,Wang Ziyuan,Pan Wei

2018-01-01

Rare Metal Materials and Engineering

Abstract:(LaxYb1-x)(2)Zr2O7 (x=0, 0.5, 1.0) thermal barrier coating materials of three different components were prepared by a solid state synthesis method using zirconia, ytterbium oxide and lanthanum oxide. The relative theoretical densities are above 97% for all samples, which were prepared by pressureless sintering for mechanical properties test. The room temperature bending strength and high temperature Young's modulus of the materials were tested by a three-point bending method and a thermomechanical analysis method, respectively. The results show that LaYbZr2O7, which is a finite solid solution consisting of La2Zr2O7-based pyrochlore and Yb2Zr2O7-based fluorite with fine grains, has improved room temperature bending strength compared with pure La2Zr2O7. It also benefits the high temperature Young's modulus above 1200 degrees C.