New Strategy for High-Performance Integrated Catalysts for Cracking Hydrocarbon Fuels.
Dengfeng Ye,Lu Zhao,Shuaishuai Bai,Yongsheng Guo,Wenjun Fang
DOI: https://doi.org/10.1021/acsami.9b14285
IF: 9.5
2019-01-01
ACS Applied Materials & Interfaces
Abstract:In this study, we described the synthesis, characterization, and application of hyperbranched polymer-encapsulated metal nanoparticles (HEMNs) as integrated catalysts for supercritical cracking of hydrocarbon fuels. The metal precursor was extracted into the organic phase using a hydrocarbon-soluble hyperbranched poly(amidoamine) (CPAMAM) and then reduced in situ by NaBH4 to produce HEMNs with virtually a single-size distribution. The monitoring of the preparation process by UV-vis demonstrated the feasibility of this encapsulation approach, and the successful synthesis of three different types of HEMNs, Metal (Pd, Pt, Au)@CPAMAM, reflected the universality of this method. Compared with the existing catalyst octadecylamine-stabilized Pd nanoparticle-Pd@18N, HEMNs were superior in every aspect. The new encapsulation method allowed metal NPs to have a smaller particle size beneficial to its overall specific surface area and a higher proportion of active-surface atoms for a better catalytic activity. Moreover, the space-limiting effect of the polymer allowed the three HEMNs to be highly dispersed in decalin and exhibited admirable stability under storage tests for up to 12 months and high temperature stability tests at 180 °C. During the supercritical cracking of decalin, Pd@CPAMAM possessed much better catalytic performance than Pd@18N and CPAMAM (which can also be used as a macroinitiator). To obtain the same heat sink of 3.02 MJ/kg, the temperature could be lowered from 725 °C to 701 °C, 693 °C, 699 °C for Pd, Pt, Au HEMNs, respectively. Pt HEMEN turned out to be the best due to its excellent catalytic dehydrogenation/cracking performance, with the conversion of decalin increasing from 22.3% to 50.7% and the heat sink rising from 2.18 MJ/kg to 2.62 MJ/kg with the existence of 50ppm Pt@CPAMAM, at 675 °C. The significant enhancements were ascribed to the synergistic catalysis through the remarkable abilities of nanometals to catalyze dehydrogenation/cracking of fuel, supercritical stabilization effects from CPAMAM, and the initiation effects of hyperbranched polymer CPAMAM.