Development of 3D printable stabilized earth-based construction materials using excavated soil: Evaluation of fresh and hardened properties

Prabhath Ranjan Kumar Soda,Ashutosh Dwivedi,CM Sahana,Souradeep Gupta,Sahana C M

DOI: https://doi.org/10.1016/j.scitotenv.2024.171654

IF: 9.8

2024-03-18

The Science of The Total Environment

Abstract:Soil excavated during construction and demolition can be utilized to reduce the demand for natural sand in 3D printed constructions. This research attempts to systematically develop 3D printable stabilized earth-based materials using excavated soil (clay content of 42.5 %) as 25 % and 50 % replacement of natural sand, and examine their compressive strength, water permeable porosity, and moisture sensitivity. The effectiveness of two binder systems – Ordinary Portland Cement (OPC) and a combination of OPC and ground granulated blast furnace slag (GGBS used to replace 30 % OPC by mass), was investigated. Non-expansive clay in the soil leads to a steeper reduction in apparent viscosity, 12–15 % higher flow retention, and 50–60 % lower plastic viscosity of soil-based mixes, thus contributing to superior extrusion quality at 35–40 mm lower initial flow than OPC-sand and OPC-GGBS-sand mixes. The addition of GGBS, due to its irregular particle morphologies and interlocking effects, further enhances the shape retention of the printed layers by 8–26 % compared to OPC-soil mortars. The structural build-ups in OPC-soil and OPC-GGBS-soil mortars increase with the increase in clay content, which enabled buildability up to a height of 1.2 m compared to only 0.51–0.55 m for OPC-sand and OPC-GGBS-sand mortars. Higher water demand due to the addition of natural clay increases the porosity of 3D printed OPC-soil mortars, thereby lowering compressive strength and increasing moisture sensitivity. However, a blend of OPC and GGBS substantially reduces the moisture sensitivity of the printed mortars at 28-day age, attributed to better stabilization of clay through hydraulic and pozzolanic action of GGBS. 28-day wet compressive strength of 14–25 MPa is obtained for the printed soil-based mixes depending on the soil dosage and loading direction. In summary, the study provides a feasible solution for the 3D printing of stabilized earth structures with lower demand for natural sand and OPC.

environmental sciences