Delayed Plasticity During Spherical Nanoindentation of an Iron-Chromium-aluminum Alloy: Effect of Ferric Ion Irradiation

Y. Zhang,C. W. Li,J. L. Jiang,J. F. Gu,H. Wang,Y. D. Jia,G. Wang,X. G. An,Q. Wang,J. Lu

DOI: https://doi.org/10.1016/j.jmst.2023.04.075

2022-01-01

Abstract:Spherical nanoindentation of an iron-chromium-aluminum alloy was conducted to study the effect of ferric-ion (Fe3 +) irradiation on the time-dependent plasticity behavior in the surface layers of this alloy. It was observed that the initiation of plasticity by the appearance of displacement burst or "pop-in" event occurred after a period of waiting time in the apparent elastic regime and that Fe3 + irradiation at 360 & DEG;C and up to-0.5 displacements per atom could make it happen under the lower applied loads but with a reduced magnitude. Through the experimental data, an activation volume and activation energy were extracted for the delayed plasticity. The results show that Fe3 +-irradiation significantly reduced its acti-vation volume from -3.05b3 to-1.75b3 (where b = Burgers vector), but slightly increased its activation energy from-0.65 to-0.71 eV. On the other hand, high-resolution scanning transmission electron mi-croscopy observations reveal that the irradiation at the elevated temperature created interstitial atom pair onto the (100) habit plane that can serve as the nucleation site of a (100) dislocation loop while elim-inating the pre-existing dislocations. Consequently, it is indicated that heterogeneous nucleation of the dislocation loop was predominant in the delayed plasticity initiation of this alloy and that the nucleation of the interstitial-type dislocation loop was involved due to Fe3 +-irradiation.& COPY; 2023 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.