Abstract:In this study, Fe-45%WC hardfacing coating was applied using flux core welding wire on ductile cast iron substrate by the GTAW process. Microstructural characterization and wear performance measurements were performed at room and 400 °C. The matrix phase of the hardfaced coating contained dendrites that chemically contained Fe and other elements such as Ni and Cr, diffused from the buffer layer. In the inter-dendritic spaces, tungsten-rich Eta carbides (Fe 3 W 3 C) with fish-bone morphology as well as chromium-rich carbides (Cr 7 C 3 ) with leaf-shaped morphology were observed. The formation of eta-carbide was due to the dissolution of WC particles during the thermal effect of the hardfacing process, and the formation of Chromium carbide was caused by dilution of the chromium element from the buffer layer. For the room temperature wear test, a protective tribolayer was formed on the wear track due to the presence of graphite in ductile cast iron, which acted as a lubricant. However, this tribolayer was unable to protect the cast iron, and it was removed during the wear test at room temperature because of its low adhesion, leading to severe wear of the base metal. On the other hand, for the Fe-45% WC hardfaced coating, despite the lack of formation of the lubricant at room temperature, much better wear resistance was observed as compared to the base metal, mainly due to its higher hardness and also presence of WC reinforcing particles in its structure. For the high temperature wear test at 400 °C, due to the formation of a continuous tribolayer, with good adhesion on the wear track of base metal and hardfaced coating, higher hardness, and trapping of WC debris in the tribolayer for the Fe-45%WC hardfaced cast iron, much better wear resistance in comparison to the room temperature wear test was observed.

An Experimental Investigation on the Effect of Microstructure on Wear Characteristics of Fe-Cr-C Hardfacing Alloys

Effect of Process Parameters on Microstructure and Properties of AlCoCrFeNi-WC-WS2 Composite Coating Prepared by Laser Cladding

Effect of alloying elements on microstructure, wear, and corrosion behavior of Fe-based hardfacing

Effect of Chromium on Microstructure and Wear Resistance of Fe-Cr-C Hardfacing Alloys

Effect of Electrode Covering Composition on the Microstructure, Wear, and Economic Feasibility of Fe-C-Cr Manual Arc-Welded Hardfacings

Effect of Nano-Additives on Microstructure, Mechanical Properties and Wear Behaviour of Fe⿿Cr⿿B Hardfacing Alloy

Microstructure and wear resistance of Fe-Cr-C-Mo-V-Ti-N hardfacing layers

Microstructure and Wear Characterization of the Fe-Mo-B-C—Based Hardfacing Alloys Deposited by Flux-Cored Arc Welding

Wear characteristics of multi layer hardfacing alloys

Effect of Molybdenum on Metallurgical and Wear Properties of Fe–Cr–C Hard facing alloy

Effect of rare earth oxide nano-additives on micro-mechanical properties and erosion behavior of Fe-Cr-C-B hardfacing alloys

Characterization of Fe–C–Cr Based Hardfacing Alloys

The Effect of Nano-Additives Containing Rare Earth Oxides on Sliding Wear Behavior of High Chromium Cast Iron Hardfacing Alloys

The Effect of Primary Carbide on the Wear Resistance of Fe-Cr-C Coatings

Microstructure and Properties of Abrasive Wearability Hardfacing Welding Based on TiC-VC

Bending Strength and Wear Behavior of Fe-Cr-C-B Hardfacing Alloys with and Without Rare Earth Oxide Nanoparticles

Dry sliding wear behavior of Fe-Cr-C-B hardfacing alloy modified with nano-CeO2 and its mechanisms of modification

An Investigation on Room and High Temperature Wear Performance of Fe-45%WC Hardfaced Coating Applied on Ductile Cast Iron

Study of Work Function and Dry Sliding Wear Behavior of Fe-Based Hardfacing Alloys with and Without Nano Rare Earth Oxides

Effect of Cr and W on microstructure and wear resistance of arc additive manufactured flux-cored wire for railway wheels

Influence of Cu and Co addition on metallurgical and wear characteristics of AlCrFeNi high entropy alloy