Abstract:This study deals with the structural changes occurring in a Mo-reach glass dedicated to the confi nement of Moreach radioactive waste that contains different contents of Cs2O oxide, ranging from 0.3 to 0.6 wt.%. The glass synthesis was carried out by the double melting method at 1380°C, followed by a stage of 2 h at 600°C. Neodymium was an actinide simulator. The glasses were characterized by their physical and microstructural properties using different spectroscopic techniques. As the experiment shows, the glass geometrical density varies between 1.96 and 2.75 g/cm3. X-ray diffraction (XRD) analysis shows amorphous features, with traces of crystalline germs, identified as the CaMoO4 powellite phase, which probably formed during glass cooling. Fourier transform infra-red (FTIR) analysis reveals the main chemical bounds in the glasses: Si–O–Si and O–Si–O in SiO4, B–O–B in BO3, and Al–O– Al in AlO4. The addition of Cs2O raises the rate of polymerization in the glass network and then decreases the number of no-bridged oxygens (NBO). Raman spectroscopic analysis reveals the absorption bands of in CaMoO4. It shows that the Mo environment is altered by the addition of increasing contents of Cs2O in the glass. This is evidenced by the absorption bands shifts at 319, 792, and 844 cm–1. The absorption band located at 700 cm–1, ascribed to the elongation of SiO4 and AlO4, is attenuated for 0.4 and 0.6% of the Cs2O content. It shifts to 680–900 cm–1 due to the glass high Mo content but increases in intensity with the Cs2O content, thus disturbing the alkali positions of Ca and Na, with Cs remaining soluble in the glass. One can conclude that a little rise in the Cs2O content inhibits the phase separation of both Na and Ca molybdates. The glasses analyses do not show particular changes in the lanthanide valences, which are probably in a +III oxidation state. The addition of Cs2O in this kind of glass network remains an issue with respect to the coherence of its microstructure. However, about 0.6 wt.% of Cs2O has been incorporated in the glass network, with no Cs2O phases segregation.

Synthesis and Characterization of Powellite-Borosilicate Glass-Ceramic for Immobilization of Mo-Rich Nuclear Waste

Synthesis and characterization of cerium monazite phosphate glass‐ceramic for immobilization of nuclear waste salt

Pyrochlore glass-ceramics for the immobilization of molybdenum-99 production wastes: Demonstrating scalability and flexibility to waste stream variance

Effect of Nd 2 O 3 dosages and melting temperatures on pyrochlore borosilicate glass-ceramics immobilization

Rapid solidification synthesis of novel (La,Y)<sub>2</sub>(Zr,Ti)<sub>2</sub>O<sub>7</sub> pyrochlore-based glass-ceramics for the immobilization of high-level wastes

Immobilize Nd2O3 as simulated nuclear waste in silicate-apatite glass-ceramics

Rapid solidification synthesis of novel (La,Y)2(Zr,Ti)2O7 pyrochlore-based glass-ceramics for the immobilization of high-level wastes

Immobilization of a simulated HLW in phosphate based glasses/glass-ceramics by melt-quenching process

Effect of varying Nd<sub>2</sub>O<sub>3</sub> contents on the structure and mechanical properties of the radioactive waste form: aluminosilicate glass-ceramics

Effect of the nature of alkali and alkaline-earth oxides on the structure and crystallization of an aluminoborosilicate glass developed to immobilize highly concentrated nuclear waste solutions

Microstructure and leach rates of apatite glass-ceramics as a host for Sr high-level liquid waste

Microstructural Analysis of a Glass Dedicated to the Radioactive Waste Confinement by Raman and FTIR Spectroscopy

Ceramic Mineral Waste-Forms for Nuclear Waste Immobilization

Structural characterization of SiO2-Na2O-CaO-B2O3-MoO3 glasses

Synthesis and characterization of sodium-aluminophosphate based glass-ceramics containing NZP phase for HLW immobilization

Effect of Mass Fraction of CeO2 on Structure of Zirconolite-based Glass-ceramics

Synthesis of glass composite material with bismuthate glass powder and zeolite-4A for immobilization of iodine waste

Effects of MoO3 and Nd2O3 on the structural features, thermal stability and properties of iron-boron-phosphate based glasses and composites

Converting natural metamorphic granite and simulated actinide oxide to aluminosilicate glass for nuclear waste immobilization

Structure, Mechanical, and Chemical Performance Evolution of Aluminosilicate Glass Modified by Nd 2 O 3

Effects of heat treatment temperature and CeO2 content on the phase composition, structure, and properties of monazite phosphate-based glass-ceramics