Influence of post-thermal treatment on characteristics of polycrystalline hybrid halide perovskite nanoparticles thin film
Simeon Amole,Oluwaseun Adedokun,Olusola Akinrinola,Olumuyiwa Aderemi Oyekanmi,Festus Akintunde Ojeniyi,Adekunle Kazeem Dauda,Ayodeji Oladiran Awodugba
DOI: https://doi.org/10.1186/s40807-024-00124-0
2024-08-18
Sustainable Energy Research
Abstract:A three-dimensional organic–inorganic hybrid halide perovskite (CH 3 NH 3 PbI 2 Br) nanoparticle film was synthesized using solution process in one step. Precursors' stoichiometry was used to prepare methylammonium bromide and lead (II) bromide in dimethyl formamide. The synthesized CH 3 NH 3 PbI 2 Br solution was spin coated on cleaned ITO prepatterned glass substrate at 2000 rpm. In addition, the influence of post-thermal treatment on the deposited nanoparticles films was evaluated by studying the structural, optical and morphological properties using X-ray Diffraction (XRD), Fourier Transform Infrared (FTIR) spectrometry, UV–visible spectrophotometry, Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM). The average crystallite sizes were calculated to be ~ 8.0, ~ 9.4, ~ 11.3 and ~ 13.1 nm of as-prepared and annealed films at 400, 500 and 600 °C, respectively. Besides, the bandgaps of 2.22 eV, 1.96 eV, 1.89 eV and 1.63 eV were extrapolated for as-prepared and annealed films at 400 °C, 500 °C and 600 °C, respectively. From J–V curves, the Jsc values of 9.4, 10.6, 11.7 and 12.8 mAcm −2 , FF values of 56.99%, 57.25%, 58.94% and 59.26% and PCE values of 2.99%, 3.49%, 3.96% and 4.39% were calculated for as-prepared and annealed CH 3 NH 3 PbI 2 Br films at 400 °C, 500 °C and 600 °C, respectively. The percentage enhancement values of 14.32%, 24.49% and 31.89% compared to as-prepared CH 3 NH 3 PbI 2 Br film. Hence, post-thermal treatment of organic–inorganic halide perovskite material improved its photoconversion efficiency without sacrificing its dimensionality.