Abstract:As substrates for surface-enhanced Raman spectroscopy (SERS), novel core/shell composite nanofiber films were prepared by coaxial electrospinning. The shell comprised Au@silicate nanohybrids, i.e., Au nanoparticles (AuNPs) immobilized in silicate nanosheets via electrostatic attraction. The polyvinyl alcohol (PVA) core provided mechanical support for the uniformly dispersed Au@silicate nanohybrids. Transmission electron microscopy revealed that the AuNPs (particle size: 25–30 nm) immobilized on the silicate nanosheets were uniform and spherical. The core/shell composite nanofiber film had a three-dimensional network structure owing to its formation via random deposition. The core/shell composite nanofibers achieved the same SERS sensitivity as the uniaxially electrospun nanofibers, despite their significantly lower AuNP content. The ultimate tensile strength of the Au@silicate nanohybrid shell layer increased 1.5-fold. The SERS enhancement factor (EF) of the uniaxially electrospun nanofiber was 4.1 × 104, compared to 1.7 × 105 for the coaxially electrospun nanofiber. These nanofibers are applicable in environmental, food safety, and biomedical fields, affording a detection limit of 10−7 M and an EF of 2.5 × 105 for Direct Blue 200 (industrial dye) and detection limits lower than 10−6 M for paraquat (pesticide) and adenine (biomolecule). The Au@silicate/PVA core/shell composite nanofibers are prospectively applicable in portable, flexible, freestanding, and stable SERS substrates for large-scale fabrication. Films prepared using the Au@silicate/PVA core/shell composite nanofibers are less susceptible to the “coffee ring” effect observed in conventional droplet coatings, improving SERS analysis reproducibility and uniformity. The developed SERS substrate has wide utility for improving sensor technologies for environmental, food safety, and biomedical applications.

Nanoparticle Assemblies: Controlled Assemblies of Gold Nanorods in PVA Nanofiber Matrix As Flexible Free‐Standing SERS Substrates by Electrospinning (small 5/2012)

Controlled Assemblies of Gold Nanorods in PVA Nanofiber Matrix As Flexible Free‐Standing SERS Substrates by Electrospinning

Simple and rapid synthesis of ultrathin gold nanowires, their self-assembly and application in surface-enhanced Raman scattering.

Co-assembly of Au Nanorods with Ag Nanowires Within Polymer Nanofiber Matrix for Enhanced SERS Property by Electrospinning.

Self-assembling of nanocubes and nanoparticles

Coaxial Electrospinning of Au@silicate/poly(vinyl Alcohol) Core/shell Composite Nanofibers with Non-Covalently Immobilized Gold Nanoparticles for Preparing Flexible, Freestanding, and Highly Sensitive SERS Substrates Amenable to Large-Scale Fabrication

Assembling of gold nanorods by femtosecond laser fabrication

Surface-enhanced Raman spectroscopy in 3D electrospun nanofiber mats coated with gold nanorods

Macroscopic Assembly of Gold Nanorods into Superstructures with Controllable Orientations by Anisotropic Affinity Interaction.

Large-scale synthesis of flexible free-standing SERS substrates with high sensitivity: electrospun PVA nanofibers embedded with controlled alignment of silver nanoparticles.

Surfactantless Photochemical Deposition of Gold Nanoparticles on an Optical Fiber Core for Surface-Enhanced Raman Scattering

Facile Synthesis of Size-Controllable Gold Nanoflowers on Carbon Nanotube Sheets as High-Performance Flexible SERS Sensors

Fiber Surface Enhanced Raman Scattering Sensor Based on Patterned Biphasic Gold–silver Nanoalloys

Self-Assembly of Ultrathin Gold Nanowires and Single Walled Carbon Nanotubes As A Highly Sensitive Substrate for Surface Enhanced Raman Spectroscopy

Deposition of the fractal-like gold particles onto electrospun polymethylmethacrylate fibrous mats and their application in surface-enhanced Raman scattering

Gold Nanorods: Evaporative Self‐Assembly of Gold Nanorods into Macroscopic 3D Plasmonic Superlattice Arrays (adv. Mater. 13/2016)

Controlled Fabrication Of Nanopillar Arrays As Active Substrates For Surface-Enhanced Raman Spectroscopy

Polarization-Dependent Surface-Enhanced Raman Scattering Via Aligned Gold Nanorods in Poly(Vinyl Alcohol) Film

π-π stacking-directed self-assembly of nanoplatelets into diversified three-dimensional superparticles for high surface-enhanced Raman scattering

Tailoring nanorod alignment in a polymer matrix by elongational flow under confinement: simulation, experiments, and surface enhanced Raman scattering application.

Fabrication of photopolymer hierarchical micronanostructures by coupling electrospinning and photolithography for SERS substrates