Effect of post-weld heat treatment on mechanical characteristics of AZ31 magnesium alloy welded joints
Zhifeng Yan,Hongxia Zhang,Jinwen Duan,Fei Liu,Guilei Wang
DOI: https://doi.org/10.1007/s11595-017-1732-5
2017-01-01
Journal of Wuhan University of Technology-Mater. Sci. Ed.
Abstract:Tungsten inert gas (TIG) welding was performed on 2.7 mm thick commercial extruded AZ31B magnesium alloy plates. We investigated the effect of post-weld heat treatment (PWHT) on the microstructure, mechanical properties and precipitated phase of the weld joints. The results showed that during the annealing treatment (200 °C-1 h, 250 °C-1 h, 300 °C-1 h, 350 °C-1 h, 400 °C-1 h, and 450 °C-1 h), the average grain size in the weld seam was the minimum after annealing at 400 °C for 1 hour, and then abnormally grew up after annealing at 450 °C for 1 hour. The mechanical properties enhanced when the joints were processed from 200 °C-1 h to 400 °C-1 h but sharply decreased with increasing annealing temperature. In contrast to the annealing treatment, solution treatment (250 °C-10 h, 300 °C-10 h, 350 °C-10 h, 400 °C-10 h, and 450 °C-10 h) exhibited a better ductility but a slight deterioration in tensile strength. Especially speaking, no eutectic compounds (such as Mg 17 Al 12 ) were observed in the weld seam. The supersaturated Al atoms were precipitated in a coarse spherical shape dispersed in the weld seam. The precipitated Al atoms dissolved in the matrix substances at the condition (400 °C-1 h) or (250 °C-10 h). The solution treatment caused grain coarsening and precipitated Al atoms dissolved in the weld seam substantially, which resulted in a drop in micro-hardness at the weld seam compared to the area of the annealed joints.