Nano-precipitation Behavior and Mechanical Properties of Ti-containing Fe–12Mn–9Al–3Cr-1.4C Medium-Mn Lightweight Steel

Junye Zhou,Jianlei Zhang,Conghui Hu,Yuxiang Liu,Zhuangzhuang Ma,Changjiang Song,Qijie Zhai

DOI: https://doi.org/10.1016/j.msea.2023.145088

IF: 6.044

2023-01-01

Materials Science and Engineering A

Abstract:The role of Ti in lightweight steel has been widely concerned due to its influence on the precipitation of nanoparticle and its inherent low density. In this work, the nano-precipitation behavior and mechanical properties of Ti-containing Fe-12Mn-9Al-3Cr-1.4C-xTi (wt.%, x = 0.02/0.04) medium-Mn lightweight steels were systematically investigated. It was found that the increase of 0.02 wt% Ti content had little influence on the two-phase structure of ferrite and austenite. TEM characterization revealed that Ti could suppress the precipitation and growth of & kappa;-carbide in austenite while promoting the precipitation of TiC particle. Based on thermodynamics and first-principles calculations, the suppression of & kappa;-carbide precipitation by the Ti element resulted from the increased formation energy of & kappa;-carbide and the decreased diffusion coefficient of C in austenite. The reduction of & kappa;-carbide decreased the precipitation strengthening in lightweight steels. However, the precipitation of TiC particle not only resulted in additional strength, but also refined the austenite grain and introduced a large number of dislocations, improving the grain boundary strengthening and dislocation strengthening. For the aged lightweight steels at 450-550 degrees C for 3 h, the increase of 0.02 wt% Ti content mainly affected the precipitation strengthening of & kappa;-carbide and dislocation strengthening. Especially, when the ageing temperature exceeded 500 degrees C, the precipitation strengthening of & kappa;-carbides became the primary factor contributing to the reinforcement of lightweight steels.