Crack Inhibition and Mechanical Property Enhancement of a CM247LC Alloy Fabricated by Laser Powder Bed Fusion Through Remelting Strategy

Linqing Liu,Di Wang,Guowei Deng,Changjun Han,Heng Zhou,Chaolin Tan,Yu Long,Zhenyu Liu,Mina Zhang,Chao Yang,Yongqiang Yang

DOI: https://doi.org/10.1016/j.matchar.2024.114073

IF: 4.537

2024-01-01

Materials Characterization

Abstract:High cracking susceptibility arising from the high thermal gradients is a critical issue of high gamma '-fraction Ni -base superalloys fabricated by laser powder bed fusion (LPBF). Here in, laser remelting was used to inhibit cracking and enhance the strength-ductility synergy of additively manufactured CM247LC alloy by LPBF. The effects of laser remelting with different energy densities and scan strategies on microstructure, cracking behavior and mechanical properties of LPBF-processed CM247LC superalloy were systematically investigated. The crack inhibition mechanisms of laser remelting during the LPBF process were revealed. Low energy density of remelting and scan strategy with a rotation of 90 degrees between remelting and prior melting were promising for decreasing the crack density. The crack inhibition caused by laser remelting could be attributed to the partial elimination of defects ( e.g. , lack-of-fusion pores), the mitigation of the segregation of elements, the backfilling of the grain boundaries and liquid film, and the reduction of the residual stress and the high-angle grain boundaries (HAGBs). Enhanced mechanical strength and ductility (ultimate tensile strength of 1280 MPa, yield strength of 885 MPa, and elongation of 11.9%) of LPBF-processed CM247LC samples were obtained by optimized-remelting parameters. This work demonstrated the potential of laser remelting in improving the printability of high gamma '-fraction Nibase superalloys fabricated by LPBF.