Unveiling the Role of Mixing in Oxygen Vacancy Formation and Metal Dispersion During Co-Precipitation Synthesis of Catalysts in Microreactor

Qiangqiang Xue,Binhang Yan,Yujun Wang,Guangsheng Luo

DOI: https://doi.org/10.1016/j.ces.2023.118942

IF: 4.7

2023-01-01

Chemical Engineering Science

Abstract:Oxygen vacancy concentration and metal dispersion are critical in the performance of metal oxide-supported metal nanoparticle (NP) catalysts. Herein, we unveil the effect of mixing on the microstructure formation of catalysts during co-precipitation synthesis in a microreactor based on a single-phase flow. The two characteristics were separately studied using Ce0.9Y0.1O2 and Ni-Al2O3 systems, Raman spectroscopy, and TEM techniques. A quasi-linear dependence between the ratio of lattice defects to lattice oxygen ((Ov + Oh)/F-2g) and segregation index X-s (i.e., (O-v + O-h)/F-2g = 5.8Xs + 0.2) and a negative correlation between Ni dispersion and X-s were determined, suggesting that the high and uniform supersaturation environment induced by efficient micromixing was favorable for the formation of crystals with abundant vacancies and small sizes. The H2O-TPSR and C3H6-TPSR experimental results demonstrated that the high oxygen vacancy concentration and Ni dispersion were beneficial to activation of O-H, C-C, and C-H bonds, respectively. Moreover, the Ni dispersion ability of CYO-Re-930 with abundant oxygen vacancy obtained at X-s = 0.003 was superior to that of CYO-Re-23, resulting in the better n-dodecane steam reforming (SR) performance of Ni/CYO-Re-930 catalyst (85.5 mol(Dodecane).mol(Ni)(-1).h(-1)). This study highlights the role of mixing in the structural formation of doped ceria and supported nickel synthesized by co-precipitation at the microscale and provides a promising approach for the continuous synthesis of catalysts with tunable oxygen vacancy concentrations and metal dispersions.