Abstract:B4C ceramics have been widely used in armor plate and cutting tools due to their high hardness. However, their poor sintering performance and low fracture toughness have limited their extended applications. In order to solve these problems, B4C@TiB2 composite powders with core‐shell structure were prepared by a sol‐gel method using B4C and TiCl4 as raw materials and then sintered by spark plasma sintering. The composite powders were characterized by X‐ray diffraction (XRD), X‐ray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM). The mechanical properties of B4C ceramics were tested by indentation and three‐point bending methods. The results showed that the B4C@TiB2 composite powders exhibited a tight core‐shell structure, and the chemical bonds on the surface were mainly B–C and B–Ti bonds. When the molar ratio of B4C:TiCl4 was 2:1, the relative density and bulk density of B4C ceramics reached 96.2% and 2.92 g/cm3, respectively. Because of the good sintering performance of the B4C@TiB2 composite powders, the Vickers hardness and fracture toughness reached 26.6 GPa and 5.22 MPa·m1/2, respectively. The bending strength reached a maximum of 570 MPa. The excellent fracture toughness can be attributed to crack deflection, crack branching, and the residual thermal stress of the core‐shell structure. This article is protected by copyright. All rights reserved

B4C-TiB2 Composite Ceramics with Ultra-High Fracture Toughness Fabricated by Spark Plasma Sintering

Effect of TiB_2 content on microstructure and mechanical properties of in-situ fabricated TiB_2/B_4C composites

Toughening mechanism of B4C/TiB2 ceramic materials by in situ reaction via spark plasma sintering

Microstructure and mechanical behaviour of transient liquid phase spark plasma sintered B4C–SiC–TiB2 composites from a B4C–TiSi2 system

Microstructures and mechanical properties of TiB2 composite ceramics with co-addition of Ti and TiC fabricated by SPS

Enhancement mechanical properties of in-situ preparated B4C-based composites with small amount of (Ti3SiC2+Si)

The improvement mechanism of mechanical properties of B4C ceramics by constructing core‐shell powders

B4C-SiC skeleton reinforced graphite composites with excellent mechanical properties

Preparation of dense B4C ceramics by spark plasma sintering of high-purity nanoparticles

High hardness and high fracture toughness B4C-diamond ceramics obtained by high-pressure sintering

B4C‒TiB2 composite with modified microstructure and enhanced properties from optimal size coupling of raw powders

Integrated preparation of B4C–TiB2 multilayer graded ceramics with high hardness and high toughness

Microstructure, mechanical properties and thermal shock behavior of h-BN-SiC ceramic composites prepared by spark plasma sintering

Microstructure and mechanical properties of TiB2–B4C ceramics fabricated by hot-pressing

Microstructure and Properties of a Graphene Platelets Toughened Boron Carbide Composite Ceramic by Spark Plasma Sintering

Planar shock compression of spark plasma sintered B4C and B4C–TiB2 ceramic composites

Spark plasma sintering and hot pressing of ZrB2–SiCW ultra-high temperature ceramics

The Fabrication and Mechanical Properties of SiC/ZrB2 Laminated Ceramic Composite Prepared by Spark Plasma Sintering

Enhanced mechanical properties and thermal shock resistance of Cf/ZrB2-SiC composite via an efficient slurry injection combined with vibration-assisted vacuum infiltration

Microstructures and mechanical properties of B4C‐SiC and B4C‐SiC‐TiB2 ceramic composites fabricated by hot pressing