Reliability analysis and compressibility correction of mercury intrusion porosimetry experiments for low-medium-rank coals

SONG Dangyu,ZHAO Yuwei,LI Yunbo,YU Zhen

DOI: https://doi.org/10.3969/j.issn.1001-1986.2023.05.004

2023-01-01

Abstract:Low-medium rank coals have soft texture and exhibit significant compressibility under high pressure, so it is controversial whether the reliable pore structure can be determined using mercury intrusion porosimetry（MIP）. Four low-medium rank coal samples were selected to conduct the high-pressure mercury injection test. By comparing the intrusion curves of different particle size samples, studying the macroscopic and microscopic characteristics before and after mercury intrusion, and establishing a correction method for high-pressure mercury intrusion volume, the reliability of MIP experiments in determining the pore structure of low-medium rank coals was investigated.The results showed that:（1） columnar samples can retain more primary fissures and effectively avoid the intergranular and pockmark effects in the low-pressure stage, making them more suitable for MIP testing of low-medium rank coals;（2） no destructive phenomenon after highpressure mercury intrusion was found with naked eye and Scanning Electron Microscopy（SEM）; the high mercury intrusion capacity was mainly due to the coal matrix compressibility. After compression correction, the pore volume measured by MIP was consistent with that measured by low-temperature N 2 adsorption, the difference in pore volume between MIP and N 2 adsorption in the range of 6-100 nm was reduced by 29.87%-55.49%, indicating that MIP can be applied to determine the pore structure of low-to medium-rank coals;（3） to correct the coal matrix compressibility at high pressure stages, a cumulative compression correction method was established, and after correction of data above 20 MPa, the mercury intrusion volume decreased by 0.017 0-0.032 3 mL/g, which was more consistent with the pore volume of nanopores determined by low-temperature N 2 adsorption experiments;（4） the pore volume of low-medium rank coals mainly comes from macropores, and there are significant differences in pore development between lignite and long-flame coal. The mercury intrusion pore volume of lignite was 0.168 7 cm~3/g, while that of long-flame coal ranged from 0.027 2 to 0.072 0 cm~3/g. For samples with particularly developed pores, plant tissue pores were the main source of pore volume.