Co-construction of microstructure evolution and wear resistance of in-situ TiBw/TA15 composites with network structure
Yunbin Lu,Yangju Feng,Wei Wang,Wenke Wang,Jianlei Yang,Wenzhen Chen,Guorong Cui,Dongdong Zhuang,Hongyang Cao
DOI: https://doi.org/10.1016/j.matchar.2023.113475
IF: 4.537
2023-11-19
Materials Characterization
Abstract:To further improve the wear resistance of titanium alloy, titanium matrix composites with network distributed TiBw were fabricated. Microstructure evolution and wear mechanism of TA15 alloy and 5 vol% TiBw/TA15 composites were investigated at the temperature of 25 °C and 600 °C. The wear rate of TiBw/TA15 composites at 600 °C was only 7.2 × 10 −5 mm 3 /(N·m). Compared to TA15 alloy, the wear rate of composites decreased by 17.2% at room temperature and 38.4% at high temperature. A novel approach was used to investigate the enhancement role of reinforcement on wear resistance of composites: co-construction of subsurface microstructure evolution and wear resistance through multi-angle observation. The results showed that the improvement of the wear resistance at room temperature was attributed to the TiBw, which enhanced work hardening and improved thermal conductivity. During high- temperature wear process, the TiBw effectively hindered dislocation movement and promoted the DRX, which decreased the stress concentration caused by severe plastic deformation.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing