Abstract:The selective catalytic reduction (SCR) of NOx with hydrogen is an attractive strategy for NOx removal when H 2 is used as sustainable fuel in combustion engines. However, the pathway suffers from a strong overconsumption of H 2 via direct oxidation to water. In order to improve the understanding of the SCR mechanism with H 2 as the reductant, the state of the active metal, the reactive surface intermediates, and the conditions which are suited for efficient SCR need to be uncovered. A 1%Pd/5%V 2 O 5 /20%TiO 2 -Al 2 O 3 catalyst was investigated using operando X-ray absorption spectroscopy (XAS) and diffuse reflectance infrared Fourier-transform spectroscopy (DRIFTS) to track the temperature dependent structure and state of Pd, as well as its gradients and surface intermediates. XAS shows that NO reduces oxidized Pd, forming metal-support interfacial nitrates according to DRIFTS. Partially reduced Pd becomes oxidized by reducing interfacial NOx species to Pd-nitrosyls. Limitations for the H 2 -SCR of NOx arise from the balance of adsorbed Pd-NO and activated H 2 , which is dependent on Pd state. The bulk metallic Pd which forms above 250 °C causes a runaway activation of H 2 , further reduction of Pd, and loss of SCR activity on Pd. The highest activity occurs when Pd is oxidized enough to promote metal-support interfacial nitrates and also reduced enough to convert these nitrates to Pd-nitrosyls. The storage of NOx and formation of NH x on vanadia-titania permits conversion of NO at high temperatures, but does not counteract the deactivation of Pd. In conclusion, activation of H 2 is favored on metallic sites, but must be moderated to allow for PdO being present as well.

TiO2 Coating on SiO2 Nanosphere Supported Pd Catalyst for the H2–SCR of NOx in the Presence of Oxygen

Selective catalytic reduction of NOx by H2 over Pd/TiO2 catalyst

Selective catalytic reduction of NOx by H2 over Na modified Pd/TiO2 catalyst

Unraveling the Promotional Effect of Co on the Pd/TiO2 Catalyst for H2-SCR of NOx in the Presence of Oxygen

Selective catalytic reduction of NOx by H2 over a novel Pd/FeTi catalyst

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

Fe2O3@SiTi Core-Shell Catalyst for the Selective Catalytic Reduction of NOx with NH3: Activity Improvement and HCl Tolerance

Selective Catalytic Reduction of NO x with CH 4 over the In/Sulfated TiO 2 Catalyst

Negatively Charged Single-Atom Pt Catalyst Shows Superior SO 2 Tolerance in NO x Reduction by CO

Selective Catalytic Reduction of NOx with CH4 over the In/Sulfated TiO2 Catalyst

Elucidating the Role of the State of Pd in the H 2 -SCR of NOx by Operando XANES and DRIFTS

Negatively Charged Single-Atom Pt Catalyst Shows Superior SO2 Tolerance in NOx Reduction by CO

Selective catalytic reduction of nitrogen oxides by methane over Ni/H-USY catalysts

Novel Pd–Au/TiO2 Catalyst for the Selective Catalytic Reduction of NOx by H2

High Performance Iridium Loaded on Natural Halloysite Nanotubes for CO-SCR Reaction

Ti species regulated CuO/CeO2 catalyst for efficient simultaneously NH3-SCR denitration and CO oxidation under oxygen-rich conditions

Unveiling the Significant Promoting Effect of SO2 on Ir/SiO2 Catalyst for the CO-SCR of NOx in the Presence of O2

Improved activity and significant SO2 tolerance of Sb-Pd-V oxides on N-doped TiO2 for CB/NOx synergistic degradation.

Flexible monolithic Pt/CuO-Fe2O3/TiO2 catalysts integrated on Ti mesh for efficient NO removal via CO-SCR reaction

One-step synthesized SO42–-TiO2 with exposed (001) facets and its application in selective catalytic reduction of NO by NH3

Investigating the Role of H4SiW12O40 in the Acidity, Oxidability and Activity of H4SiW12O40-Fe2O3 Catalysts for the Selective Catalytic Reduction of NO with NH3