Abstract:In this paper, the crack problem of a certain type of rotary drill pipe in use is studied, and a simplified calculation method for the fatigue life of rotary drill pipe is proposed. The bench test device built can be used for the fatigue life test of all tubular structures by analogy. The calculation method of fatigue life of rotary drill pipe is studied through field test and bench test of drill pipe. Firstly, a simplified model of the drill pipe was established with the outer rod of the rotary drill pipe as the research object, and the model was verified. Then, the difference between the hot spot stress extrapolation method recommended by the IIW standard and the DNV standard was compared, and the hot spot stress of the drill pipe was calculated by the two-point linear extrapolation method recommended by the IIW standard, and the equivalent fatigue limit of the drill pipe was obtained by the Von Mises criterion. Finally, the equivalent load was deduced according to the stress level of the actual work test, and the constant amplitude load test was carried out on the bench, and the fatigue life of the drill pipe under the constant amplitude load was obtained. The results show that both the simplified model of the drill pipe and the bench test drill pipe can well reflect the stress level of the field test. The rotary drill pipe mainly bears torsional load, and the crack position of the bench test corresponds to the actual drill pipe crack position. The fatigue life of drill pipe is calculated by applying the Von Mises criterion and Basquin's SN curve power function. The calculated fatigue life is consistent with the results of the bench test. The calculation method can be well applied to the life analysis problem of multiaxial fatigue of large structural parts.

Safe Life Estimation of Coke Drum in Service Environment

A New Empirical Life Prediction Model For 9-12%Cr Steels Under Low Cycle Fatigue And Creep Fatigue Interaction Loadings

Further Investigation Into the Damage Tolerance of Different Coke Drum Support Skirt Designs

A fatigue life prediction approach to interior cracking induced high cycle and very high cycle fatigue for surface‐carburized steels

Fatigue Life Calculation Method of 4130X High Pressure Hydrogen Storage Cylinder With Initial Crack Defect

Safety evaluation of deformed coke drum with nested stress at cold spot

Evaluation of Fatigue Life Prediction Models and Investigation of Fracture Mechanisms of Mild Steel

Fatigue life analysis of rotary drill pipe

A novel very-high-cycle-fatigue life prediction model with interior microstructure induced cracking behavior of Inconel-713C superalloy at 25 °C, 750 °C and 1000 °C

Stress and Fatigue Life Monitoring of High Temperature Bearing Elements Based on the Solution of Inverse Conduction Problem

Life prediction and damage analysis of creep-fatigue combined with high-low cycle loading by using a crystal plasticity-based approach

The cyclic response behavior, failure mechanism, and life prediction model of 9% Cr‐based steel under different strain ratios in the low cyclic fatigue regime at 430°C

A New Method for Low Cycle Fatigue Life Prediction

Low Cycle Fatigue Damage Evolution & Life Estimate of 10CrMo910 Steel

Thermal stress analysis of lining plate for dry quenching

Numerical Simulation of the Transient Heat Transfer of Coke Drums and Study on the Characteristic of Stress Filed

Fracture Mechanics Applied in Service Life Analysis of the Fast Peak Shaving Boiler Drum

Fatigue failure analysis and life prediction of wheel load local area of ladle crane

Simple Predicting Method for Fatigue Crack Growth Rate Based on Tensile Strength of Carbon Steel

Fatigue Life Investigation of a High Pressure Inner Casing under In-Service Conditions

A new data-driven probabilistic fatigue life prediction framework informed by experiments and multiscale simulation