Effect of Cu addition on microstructure, texture and magnetic properties of 6.5 wt% Si electrical steel

Zhaoyang Cheng,Jing Liu,Zhidong Xiang,Juan Jia,Olena Volkova,Macro Wendler

DOI: https://doi.org/10.1016/j.jmmm.2020.167471

IF: 3.097

2021-02-01

Journal of Magnetism and Magnetic Materials

Abstract:<p>The effect of Cu addition in the range of 0–1.0 wt.% on the magnetic induction and iron loss of 6.5 wt.% Si electrical steel is investigated. The microstructure and texture of the steels are also analysed to reveal the mechanisms by which their magnetic properties after annealing are affected by Cu addition. Cu addition up to 0.7 wt.% is found to increase magnetic induction <span class="math"><math>B50</math></span> although the increase is very small due to the formation of η-fiber texture. The iron loss of 6.5 wt.% Si electrical steel decreases with increasing Cu addition to up to 0.5 wt.%, but increases with further Cu addition. When Cu addition is increased to 0.7 wt.%, the iron loss for this steel becomes higher than for that without Cu addition. Microstructural analysis suggests that Cu addition of up to 0.5 wt.% can promote the recrystallization during annealing and increase the recrystallized grain size, leading to a decrease in iron loss. With further increase in Cu addition, especially beyond 0.7 wt.%, large numbers of fine ε-Cu precipitates form in the microstructure during warm-rolling, which inhibit grain growth during annealing. This is the main reason for the observed increase in iron loss when Cu addition is over 0.5 wt.% Cu. The Cu addition range for achieving the optimum magnetic properties for 6.5 wt.% Si electrical steel is 0.3 – 0.5 wt.%.</p>

materials science, multidisciplinary,physics, condensed matter